Combined internal donor system for ziegler-natta polyolefin catalysts and methods of making and using same

ABSTRACT

Solid catalyst components are disclosed including titanium, magnesium, halogen and an internal electron donor compound having a combination of internal electron donor compounds including at least one 1,8-naphthyl diester and at least one secondary internal donor compound selected from alkyl 2-alkoxy-1-naphthoates, alkyl 2-alkoxybenzoates, alkyl 2,6-dialkoxybenzoates, (2-alkoxyphenyl)(pyrrolidin-1-yl)alkanones, dialkyl phthalates, alkyl alkionates, and dialkyl cyclohexane-1,2-dicarboxylates, and catalyst systems containing the catalyst solid components, organoaluminum compounds, and organosilicon compounds. Further, methods of making the catalyst components and the catalyst systems are disclosed as well as methods of polymerizing or copolymerizing alpha-olefins using the catalyst systems.

TECHNICAL FIELD

The present disclosure relates generally to solid catalyst components for olefin polymerization. In particular, the solid catalyst components comprise titanium, magnesium, halogen and a combination of internal electron donor compounds, wherein said combination of internal electron donor compounds comprises at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII). The present disclosure further relates to catalyst systems containing the solid catalyst components, methods of making the solid catalyst components and the catalyst systems, and methods of polymerizing or copolymerizing alpha-olefins using the catalyst systems.

BACKGROUND

Polyolefins are a class of polymers derived from simple olefins. Known methods of making polyolefins involve the use of Ziegler-Natta polymerization catalysts. These catalysts polymerize vinyl monomers using a transition metal halide to provide a polymer with an isotactic stereochemical configuration.

Two types of Ziegler-Natta catalyst systems are traditionally used for the polymerization or copolymerization of olefins. The first, in its broadest definition, comprises TiCl₃ based catalysts components obtained, for example, by the reduction of TiCl₄ with Al-alkyls, used in combination with Al-compounds such as diethylaluminum chloride (DEAC). Despite the modest properties of the resulting polymers in terms of isotacticity, the catalysts are characterized by a very low activity which results in the presence of large amounts of catalytic residues in the polymers.

The second type of catalyst system comprises a solid catalyst component, constituted by magnesium dihalide on which are supported a titanium compound and an internal electron donor compound. In order to maintain the high selectivity for an isotactic polymer product, a variety of internal electron donor compounds must be added during the catalyst synthesis. Conventionally, when a higher crystallinity of the polymer is required, an external donor compound is also added during the polymerization reaction. Both the internal and external electron donor compounds become indispensable compositions of catalyst components.

During the past 30 years, numerous supported Ziegler-Natta catalysts have been developed which afford a much higher activity in olefin polymerization reactions and significantly higher contents of crystalline isotactic fractions in the polymers they produce. With the development of new internal and external electron donor compounds, polyolefin catalyst systems have been continuously improved.

SUMMARY

The following presents a simplified summary to provide a basic understanding of some aspects of the presently disclosed and claimed inventive concept(s). This summary is not an extensive overview of the presently disclosed and claimed inventive concept(s). It is intended to neither identify key or critical elements of the presently disclosed and claimed inventive concept(s) nor delineate the scope of the presently disclosed and claimed inventive concept(s). Rather, the purpose of this summary is to present various concepts of the presently disclosed and claimed inventive concept(s) in a simplified form as a prelude to the more detailed description that is presented hereafter.

The present disclosure provides a solid catalyst component for use in olefin polymerization, an olefin polymerization catalyst system containing the solid catalyst component, methods of making the solid catalyst component and the catalyst system, and methods of polymerizing and/or copolymerizing olefins involving the use of the catalyst system. The solid catalyst component comprises titanium, magnesium, halogen, and a combination of internal electron donor compounds, wherein said combination of internal electron donor compounds comprises at least one 1,8-naphthyl diester compound represented by general formula (I):

and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II):

a compound represented by general formula (III):

a compound represented by general formula (IV):

a compound represented by general formula (V):

a compound represented by general formula (VI):

a compound represented by general formula (VII):

a compound represented by general formula (VIII):

wherein

R₁ and R₂ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₃, R₄, R₅, R₆, R₇, and R₈ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₉ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₀ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₁, R₁₂, R₁₃, R₁₄, R₁₅, and R₁₆ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₇ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₈ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₉, R₂₀, R₂₁, and R₂₂ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₂₃, R₂₄, and R₂₅ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₂₆ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₂₇, R₂₈, R₂₉, and R₃₀ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₃₁, R₃₂, R₃₃, R₃₄, R₃₅, R₃₆, R₃₇, and R₃₈ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₃₉ and R₄₀ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₄₁ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₄₂ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; and R₄₃ and R₄₄ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens.

In certain embodiments, R₁-R₄₄ are each independently selected from the group consisting of H; a halogen; and a linear or branched C₁-C₂₀ alkyl group

The term “hydrocarbyl” refers to any moiety comprising only hydrogen and carbon atoms, unless otherwise explicitly stated. A hydrocarbyl can also form a non-aromatic, such as cyclohexane, or an aromatic ring, such as a substituted or unsubstituted (C₆-C₁₀)aryl group. Examples of hydrocarbyl groups are (C₁-C₂₀)hydrocarbyl, including (C₁-C₁₀)hydrocarbyl, and including benzyl and cyclohexyl.

In an embodiment, the solid catalyst system can include a titanium compound having at least one titanium-halogen bond and the combination of internal electron donor compounds supported on a magnesium halide crystal lattice. In an embodiment, the solid catalyst system can include a titanium compound having at least one titanium-halogen bond and the combination of internal electron donor compounds supported on a magnesium dichloride crystal lattice. In an embodiment, the solid catalyst system the titanium compound is TiCl₄ or TiCl₃.

The presently disclosure provides a solid catalyst component for use in olefinic polymerization including:

a reaction product of a titanium compound,

a magnesium compound, and

a combination of internal electron donor compounds, wherein said combination of internal electron donor compounds comprises at least one 1,8-naphthyl diester compound represented by general formula (I):

and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II):

a compound represented by general formula (III):

a compound represented by general formula (IV):

a compound represented by general formula (V):

a compound represented by general formula (VI):

a compound represented by general formula (VII):

a compound represented by general formula (VIII):

wherein

R₁ and R₂ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₃, R₄, R₅, R₆, R₇, and R₈ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₉ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₀ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₁, R₁₂, R₁₃, R₁₄, R₁₅, and R₁₆ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₇ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₈ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₉, R₂₀, R₂₁, and R₂₂ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₂₃, R₂₄, and R₂₅ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₂₆ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₂₇, R₂₈, R₂₉, and R₃₀ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₃₁, R₃₂, R₃₃, R₃₄, R₃₅, R₃₆, R₃₇, and R₃₈ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₃₉ and R₄₀ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₄₁ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₄₂ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; and R₄₃ and R₄₄ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens.

In certain embodiments, R₁—R₄₄ are each independently selected from the group consisting of H; a halogen; and a linear or branched C₁-C₂₀ alkyl group

In an embodiment of the solid catalyst component, the 1,8-naphthyl diester compound of the general formula (I) is selected from the group consisting of naphthalene-1,8-diyl dibenzoate, 8-(benzoyloxy)naphthalen-1-yl 2-methylbenzoate, 8-(benzoyloxy)naphthalen-1-yl 3-methylbenzoate, 8-(benzoyloxy)naphthalen-1-yl 4-methylbenzoate, 8-(benzoyloxy)naphthalen-1-yl 2,4,6-trimethylbenzoate, 8-(benzoyloxy)naphthalen-1-yl isonicotinate, 8-(benzoyloxy)naphthalen-1-yl nicotinate, 8-(benzoyloxy)naphthalen-1-yl picolinate, 8-((cyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-((cyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-((2-methylcyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-((3-methylcyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-((4-methylcyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-(propionyloxy)naphthalen-1-yl benzoate, 8-(butyryloxy)naphthalen-1-yl benzoate, 8-(pentanoyloxy)naphthalen-1-yl benzoate, 8-(benzoyloxy)naphthalen-1-yl tetrahydro-2H-pyran-4-carboxylate, 8-(benzoyloxy)naphthalen-1-yl piperidine-4-carboxylate, and 8-(benzoyloxy)naphthalen-1-yl tetrahydro-2H-thiopyran-4-carboxylate.

In an embodiment of the solid catalyst component, the at least one secondary internal donor compound includes a compound represented by general formula (II) as selected from the group consisting of 2-methoxy-1-naphthoic acid, methyl 2-methoxy-1-naphthoate, ethyl 2-methoxy-1-naphthoate, propyl 2-methoxy-1-naphthoate, butyl 2-methoxy-1-naphthoate, pentyl 2-methoxy-1-naphthoate, hexyl 2-methoxy-1-naphthoate, heptyl 2-methoxy-1-naphthoate, octyl 2-methoxy-1-naphthoate, nonyl 2-methoxy-1-naphthoate, undecyl 2-methoxy-1-naphthoate, dodecyl 2-methoxy-1-naphthoate, tridecyl 2-methoxy-1-naphthoate, tetradecyl 2-methoxy-1-naphthoate, pentadecyl 2-methoxy-1-naphthoate, hexadecyl 2-methoxy-1-naphthoate, heptadecyl 2-methoxy-1-naphthoate, heptadecyl 2-methoxy-1-naphthoate, octadecyl 2-methoxy-1-naphthoate, nonadecyl 2-methoxy-1-naphthoate, isopropyl 2-methoxy-1-naphthoate, isobutyl 2-methoxy-1-naphthoate, isopentyl 2-methoxy-1-naphthoate, 4-methylpentyl 2-methoxy-1-naphthoate, 5-methylhexyl 2-methoxy-1-naphthoate, 6-methylheptyl 2-methoxy-1-naphthoate, 7-methyloctyl 2-methoxy-1-naphthoate, 8-methylnonyl 2-methoxy-1-naphthoate, 9-methyldecyl 2-methoxy-1-naphthoate, 10-methylundecyl 2-methoxy-1-naphthoate, 11-methyldodecyl 2-methoxy-1-naphthoate, 12-methyltridecyl 2-methoxy-1-naphthoate, 13-methyltetradecyl 2-methoxy-1-naphthoate, 14-methylpentadecyl 2-methoxy-1-naphthoate, 15-methylhexadecyl 2-methoxy-1-naphthoate, 16-methylheptadecyl 2-methoxy-1-naphthoate, 17-methyloctadecyl 2-methoxy-1-naphthoate, and 18-methylnonadecyl 2-methoxy-1-naphthoate, methyl 2-ethoxy-1-naphthoate, methyl 2-propoxy-1-naphthoate, methyl 2-butoxy-1-naphthoate, methyl 2-(pentyloxy)-1-naphthoate, methyl 2-(hexyloxy)-1-naphthoate, methyl 2-(heptyloxy)-1-naphthoate, methyl 2-(octyloxy)-1-naphthoate, methyl 2-(decyloxy)-1-naphthoate, methyl 2-(undecyloxy)-1-naphthoate, methyl 2-(dodecyloxy)-1-naphthoate, methyl 2-(tridecyloxy)-1-naphthoate, methyl 2-(tetradecyloxy)-1-naphthoate, methyl 2-(pentadecyloxy)-1-naphthoate, methyl 2-(hexadecyloxy)-1-naphthoate, methyl 2-(heptadecyloxy)-1-naphthoate, methyl 2-isobutoxy-1-naphthoate, methyl 2-(isopentyloxy)-1-naphthoate, methyl 2-((4-methylpentyl)oxy)-1-naphthoate, methyl 2-((5-methylhexyl)oxy)-1-naphthoate, methyl 2-((6-methylheptyl)oxy)-1-naphthoate, methyl 2-((7-methyloctyl)oxy)-1-naphthoate, methyl 2-((9-methyldecyl)oxy)-1-naphthoate, methyl 2-((10-methylundecyl)oxy)-1-naphthoate, methyl 2-((11-methyldodecyl)oxy)-1-naphthoate, methyl 2-((12-methyltridecyl)oxy)-1-naphthoate, methyl 2-((13-methyltetradecyl)oxy)-1-naphthoate, methyl 2-((14-methylpentadecyl)oxy)-1-naphthoate, methyl 2-((15-methylhexadecyl)oxy)-1-naphthoate, methyl 2-((16-methylheptadecyl)oxy)-1-naphthoate, methyl 2-((16-methylheptadecyl)oxy)-1-naphthoate, methyl 2-((17-methyloctadecyl)oxy)-1-naphthoate, and methyl 2-((18-methylnonadecyl)oxy)-1-naphthoate.

In an embodiment of the solid catalyst component, the at least one secondary internal donor compound includes a compound represented by general formula (III) as selected from the group consisting of butyl 2-methoxybenzoate, methyl 2-methoxybenzoate, ethyl 2-methoxybenzoate, propyl 2-methoxybenzoate, pentyl 2-methoxybenzoate, hexyl 2-methoxybenzoate, isopentyl 2-methoxybenzoate, isopropyl 2-methoxybenzoate, isobutyl 2-methoxybenzoate, 4-methylpentyl 2-methoxybenzoate, 5-methylhexyl 2-methoxybenzoate, undecyl 2-methoxybenzoate, tridecyl 2-methoxybenzoate, henicosyl 2-methoxybenzoate, 2-methoxybenzoic acid, butyl 2-hydroxybenzoate, butyl 2-ethoxybenzoate, butyl 2-propoxybenzoate, butyl 2-butoxybenzoate, butyl 2-methoxy-3-methylbenzoate, butyl 2-methoxy-4-methylbenzoate, butyl 2-methoxy-5-methylbenzoate, butyl 2-methoxy-6-methylbenzoate, butyl 3-chloro-2-methoxybenzoate, butyl 5-chloro-2-methoxybenzoate, butyl 4-chloro-2-methoxybenzoate, and butyl 2-chloro-6-methoxybenzoate.

In an embodiment of the solid catalyst component, the at least one secondary internal donor compound includes a compound represented by general formula (IV) as selected from the group consisting of methyl 2,6-dimethoxybenzoate, ethyl 2,6-dimethoxybenzoate, propyl 2,6-dimethoxybenzoate, butyl 2,6-dimethoxybenzoate, pentyl 2,6-dimethoxybenzoate, hexyl 2,6-dimethoxybenzoate, heptyl 2,6-dimethoxybenzoate, octyl 2,6-dimethoxybenzoate, nonyl 2,6-dimethoxybenzoate, decyl 2,6-dimethoxybenzoate, dodecyl 2,6-dimethoxybenzoate, octadecyl 2,6-dimethoxybenzoate, phenyl 2,6-dimethoxybenzoate, cyclohexyl 2,6-dimethoxybenzoate, pyridin-4-yl 2,6-dimethoxybenzoate, tetrahydro-2H-pyran-4-yl 2,6-dimethoxybenzoate, isopropyl 2,6-dimethoxybenzoate, isobutyl 2,6-dimethoxybenzoate, isopentyl 2,6-dimethoxybenzoate, 4-methylpentyl 2,6-dimethoxybenzoate, 5-methylhexyl 2,6-dimethoxybenzoate, 6-methylheptyl 2,6-dimethoxybenzoate, 7-methyloctyl 2,6-dimethoxybenzoate, 8-methylnonyl 2,6-dimethoxybenzoate, 9-methyldecyl 2,6-dimethoxybenzoate, butyl 2-ethoxy-6-methoxybenzoate, butyl 2-methoxy-6-propoxybenzoate, 7-methyloctyl 2-ethoxy-6-methoxybenzoate, and 7-methyloctyl 2-methoxy-6-propoxybenzoate.

In an embodiment of the solid catalyst component, the at least one secondary internal donor compound includes a compound represented by general formula (V) as selected from the group consisting of (2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (2-ethoxyphenyl)(pyrrolidin-1-yl)methanone, (2-propoxyphenyl)(pyrrolidin-1-yl)methanone, (2-butoxyphenyl)(pyrrolidin-1-yl)methanone, (2-(pentyloxy)phenyl)(pyrrolidin-1-yl)methanone, (2-(hexyloxy)phenyl)(pyrrolidin-1-yl)methanone, (2-(dodecyloxy)phenyl)(pyrrolidin-1-yl)methanone, (2-(icosyloxy)phenyl)(pyrrolidin-1-yl)methanone, (2-isopropoxyphenyl)(pyrrolidin-1-yl)methanone, (2-isobutoxyphenyl)(pyrrolidin-1-yl)methanone, (2-(isopentyloxy)phenyl)(pyrrolidin-1-yl)methanone, (2-phenoxyphenyl)(pyrrolidin-1-yl)methanone, (2-(cyclohexyloxy)phenyl)(pyrrolidin-1-yl)methanone, (2-(pyridin-4-yloxy)phenyl)(pyrrolidin-1-yl)methanone, pyrrolidin-1-yl(2-((tetrahydro-2H-pyran-4-yl)oxy)phenyl)methanone, (2-(2-ethoxyethoxy)phenyl)(pyrrolidin-1-yl)methanone, (2-(2-(ethylamino)ethoxy)phenyl)(pyrrolidin-1-yl)methanone, (2-methoxyphenyl)(2-methylpyrrolidin-1-yl)methanone, (2-chloropyrrolidin-1-yl)(2-methoxyphenyl)methanone, (2-methoxyphenyl)(3-methylpyrrolidin-1-yl)methanone, (3-chloropyrrolidin-1-yl)(2-methoxyphenyl)methanone, (2-methoxy-5-methylphenyl)(pyrrolidin-1-yl)methanone, (2-methoxy-3-methylphenyl)(pyrrolidin-1-yl)methanone, (2-methoxy-4-methylphenyl)(pyrrolidin-1-yl)methanone, (2-methoxy-6-methylphenyl)(pyrrolidin-1-yl)methanone, (5-bromo-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (3-bromo-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (4-bromo-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (2-bromo-6-methoxyphenyl)(pyrrolidin-1-yl)methanone, (5-chloro-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (3-chloro-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (4-chloro-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (2-chloro-6-methoxyphenyl)(pyrrolidin-1-yl)methanone, (5-fluoro-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (3-fluoro-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (4-fluoro-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (2-fluoro-6-methoxyphenyl)(pyrrolidin-1-yl)methanone, (5-iodo-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (3-iodo-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (4-iodo-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, and (2-iodo-6-methoxyphenyl)(pyrrolidin-1-yl)methanone.

In an embodiment of the solid catalyst component, the at least one secondary internal donor compound includes a compound represented by general formula (VI) as selected from the group consisting of dibutyl phthalate (DnBP), diisobutyl phthalate (DIBP), dioctyl phthalate (DOP), bis(2-ethylhexyl) phthalate (DEHP), bis(6-methylheptyl) phthalate (DiOP, a.k.a. diisooctylphthalate), bis(7-methyloctyl) phthalate (DINP), and bis(2-propylheptyl) phthalate (DPHP).

In an embodiment of the solid catalyst component, the at least one secondary internal donor compound includes a compound represented by general formula (VII) as selected from the group consisting of methyl acetate, ethyl acetate, propyl acetate, butyl acetate, pentyl acetate, hexyl acetate, heptyl acetate, octyl acetate, phenyl acetate, cyclohexyl acetate, isobutyl acetate, isopentyl acetate, 4-methylpentyl acetate, 5-methylhexyl acetate, 6-methylheptyl acetate, 7-methyloctyl acetate, methyl propionate, methyl butyrate, methyl pentanoate, methyl hexanoate, methyl heptanoate, methyl octanoate, methyl decanoate, methyl dodecanoate, methyl stearate, methyl benzoate, methyl cyclohexanecarboxylate, methyl 3-methylbutanoate, methyl 4-methylpentanoate, methyl 5-methylhexanoate, methyl 6-methylheptanoate, methyl 7-methyloctanoate, methyl 9-methyldecanoate, methyl 11-methyldodecanoate, and methyl 16-methylheptadecanoate.

In an embodiment of the solid catalyst component, the at least one secondary internal donor compound includes a compound represented by general formula (VIII) as selected from the group consisting of dibutyl cyclohexane-1,2-dicarboxylate, diisobutyl cyclohexane-1,2-dicarboxylate, dioctyl cyclohexane-1,2-dicarboxylate, bis(2-ethylhexyl)cyclohexane-1,2-dicarboxylate, bis(6-methylheptyl)cyclohexane-1,2-dicarboxylate, bis(7-methyloctyl)cyclohexane-1,2-dicarboxylate, and bis(2-propylheptyl)cyclohexane-1,2-dicarboxylate. In an embodiment of the solid catalyst component, at least one of R₁ and R₂ is phenyl, and at least one of R₉, R₁₀, R₁₇, R₁₈, R₂₃, R₂₄, R₂₅ R₂₆, R₃₉, R₄₀ R₄₁, R₄₂, R₄₃, and R₄₄ is a C₁-C₂₀ linear or branched alkyl group. In an embodiment of the solid catalyst component, at least one of R₃, R₄, R₅, R₆, R₇, R₈, R₁₁, R₁₂, R₁₃, R₁₄, R₁₅, R₁₆, R₁₉, R₂₀, R₂₁, R₂₂, R₂₇, R₂₈, R₂₉, R₃₀, R₃₁, R₃₂, R₃₃, R₃₄, R₃₅, R₃₆, R₃₇, and R₃₈ is H. In an embodiment, the solid catalyst component has a surface area (by B.E.T. method) between about 10 and about 1,000 m²/g.

The present disclosure provides a catalyst system for use in olefinic polymerization, comprising: (i) said solid catalyst component as described herein; (ii) an organoaluminum compound; and (iii) optionally an organosilicon compound. In an embodiment of the catalyst system, the organoaluminum compound is an alkyl-aluminum compound. In an embodiment of the catalyst system, the alkyl-aluminum compound is a trialkyl aluminum compound. In an embodiment of the catalyst system, the trialkyl aluminum compound is selected from the group consisting of triethylaluminum, triisobutylaluminum, and tri-n-octylaluminum.

The present disclosure provides a method of making a solid catalyst component for a catalyst system, including

contacting a magnesium compound and a titanium compound with a combination of internal electron donor compounds,

wherein said combination of internal electron donor compounds comprises at least one 1,8-naphthyl diester compound represented by general formula (I):

and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II):

a compound represented by general formula (III):

a compound represented by general formula (IV):

a compound represented by general formula (V):

a compound represented by general formula (VI):

a compound represented by general formula (VII):

a compound represented by general formula (VIII):

wherein

R₁ and R₂ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₃, R₄, R₅, R₆, R₇, and R₈ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₉ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₀ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₁, R₁₂, R₁₃, R₁₄, R₁₅, and R₁₆ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₇ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₈ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₉, R₂₀, R₂₁, and R₂₂ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₂₃, R₂₄, and R₂₅ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₂₆ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₂₇, R₂₈, R₂₉, and R₃₀ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₃₁, R₃₂, R₃₃, R₃₄, R₃₅, R₃₆, R₃₇, and R₃₈ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₃₉ and R₄₀ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₄₁ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₄₂ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; and R₄₃ and R₄₄ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens.

In certain embodiments, R₁-R₄₄ are each independently selected from the group consisting of H; a halogen; and a linear or branched C₁-C₂₀ alkyl group

In an embodiment of the method, the compound of the general formula (I) is selected from the group consisting of naphthalene-1,8-diyl dibenzoate, 8-(benzoyloxy)naphthalen-1-yl 2-methylbenzoate, 8-(benzoyloxy)naphthalen-1-yl 3-methylbenzoate, 8-(benzoyloxy)naphthalen-1-yl 4-methylbenzoate, 8-(benzoyloxy)naphthalen-1-yl 2,4,6-trimethylbenzoate, 8-(benzoyloxy)naphthalen-1-yl isonicotinate, 8-(benzoyloxy)naphthalen-1-yl nicotinate, 8-(benzoyloxy)naphthalen-1-yl picolinate, 8-((cyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-((cyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-((2-methylcyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-((3-methylcyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-((4-methylcyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-(propionyloxy)naphthalen-1-yl benzoate, 8-(butyryloxy)naphthalen-1-yl benzoate, 8-(pentanoyloxy)naphthalen-1-yl benzoate, 8-(benzoyloxy)naphthalen-1-yl tetrahydro-2H-pyran-4-carboxylate, 8-(benzoyloxy)naphthalen-1-yl piperidine-4-carboxylate, and 8-(benzoyloxy)naphthalen-1-yl tetrahydro-2H-thiopyran-4-carboxylate.

The present disclosure provides a process for polymerizing or copolymerizing an olefin monomer, comprising the steps of: (i) providing the catalyst system, as provided herein; (ii) polymerizing or copolymerizing the olefin monomer in the presence of the catalyst system to form a polymer or a copolymer; and (iii) recovering the polymer or copolymer.

In order to achieve the foregoing and related ends, the presently disclosed and claimed inventive concept(s) involves the features hereinafter fully described and particularly pointed out in the claims. The following description and the annexed drawings set forth in detail certain illustrative aspects and implementations of embodiments of the disclosure. These are indicative, however, of but a few of the various ways in which the principles of the presently disclosed and claimed inventive concept(s) may be employed. Other objects, advantages and novel features of the presently disclosed and claimed inventive concept(s) will become apparent from the following detailed description of the presently disclosed and claimed inventive concept(s) when considered in conjunction with the drawings and one of ordinary skill in the art would appreciate such additional objects, advantages, and novel features given in the present disclosure.

BRIEF SUMMARY OF THE DRAWINGS

FIG. 1 is a schematic diagram of an olefin polymerization system in accordance with an aspect of the presently disclosed and claimed inventive concept(s).

FIG. 2 is a schematic diagram of an olefin polymerization reactor in accordance with an aspect of the presently disclosed and claimed inventive concept(s).

FIG. 3 is a schematic diagram of a system for making impact copolymer in accordance with an aspect of the presently disclosed and claimed inventive concept(s).

FIG. 4 is an optical microscope picture of polypropylene produced with a dibutyl phthalate-naphthalene-1,8-diyl dibenzoate (“THANE”) catalyst.

FIG. 5 is a graph of catalyst activity (CE) over H₂ response for a diisooctyl phthalate-THANE donor catalyst.

FIG. 6 is a graph of melt flow index (MFI) over H₂ response for a diisooctyl phthalate-THANE donor catalyst.

FIG. 7 is a graph of xylene soluble (XS) over a ratio of Si/Ti for a diisooctyl phthalate-THANE donor catalyst.

DETAILED DESCRIPTION

The presently disclosed and claimed inventive concept(s) relates to solid catalyst components containing titanium, magnesium, halogen and a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of mono- or poly-carboxylic esters, ethers, ketones, organic compounds containing carboxylic and ether groups, organic compounds containing carboxylic groups and carbonyl groups, and organic compounds containing carboxylic groups, ether groups, and carbonyl groups.

In one embodiment, the at least one secondary internal donor compound is selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and/or (VIII) in olefinic polymerization; olefin polymerization catalyst systems containing the solid catalyst components, organoaluminums, and organosilicons; methods of making the solid catalyst components and the catalyst systems; and methods of polymerizing and/or copolymerizing olefins using the catalyst systems.

In one embodiment, the at least one secondary internal donor compound is selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII) in olefinic polymerization, including alkyl 2-alkoxy-1-naphthoates, alkyl 2-alkoxybenzoates, alkyl 2,6-dialkoxybenzoates, (2-alkoxyphenyl)(pyrrolidin-1-yl)alkanones, dialkyl phthalates, alkyl alkionates, or dialkyl cyclohexane-1,2-dicarboxylates, respectively.

An aspect of the presently disclosed and claimed inventive concept(s) is a solid catalyst component comprising titanium, magnesium, halogen and a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII). In one embodiment, the solid catalyst component comprises a titanium compound having at least one titanium-halogen bond and a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII) supported on a magnesium halide crystal lattice. The titanium compound is TiCl₄ or TiCl₃. In one embodiment, the magnesium halide crystal lattice is a magnesium dichloride crystal lattice, which is widely known by one of ordinary skill in the art as a support for Ziegler-Natta catalysts.

In certain embodiments, the solid catalyst component of the present disclosure is an active catalyst component comprising a reaction product of a titanium compound, a magnesium compound, and a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII).

The titanium compounds used in the preparation of the solid catalyst component can include, for example, a tetravalent titanium compound represented by chemical formula (1):

Ti(OR)_(g)X_(4-g)  (1)

wherein R represents a hydrocarbon group, including an alkyl group having 1 to about 20 carbon atoms, X represents a halogen atom, and 0≦g≦4. Specific examples of the titanium compound include, but are not limited to, titanium tetrahalides such as TiCl₄, TiBr₄, and TiI₄; alkoxytitanium trihalides such as Ti(OCH₃)Cl₃, Ti(OC₂H₅)Cl₃, Ti(O-n-C₄H₉)Cl₃, Ti(OC₂H₅)Br₃ and Ti(O-i-C₄H₉)Br₃; dialkoxytitanium dihalides such as Ti(OCH₃)₂Cl₂, Ti(OC₂H₅)₂Cl₂, Ti(O-n-C₄H₉)₂Cl₂ and Ti(OC₂H₅)₂Br₂; trialkoxytitanium monohalides such as Ti(OCH₃)₃Cl, Ti(OC₂H₅)₃Cl, Ti(O-n-C₄H₉)₃Cl and Ti(OC₂H₅)₃Br; and tetraalkoxytitaniums such as Ti(OCH₃)₄, Ti(OC₂H₅)₄ and Ti(O-n-C₄H₉)₄. Among these, the halogen containing titanium compounds, including titanium tetrahalides, have been found to be useful for at least one embodiment. These titanium compounds may be used individually or in solutions of hydrocarbon compounds or halogenated hydrocarbons.

The magnesium compounds used in the preparation of the solid catalyst component include halogen containing magnesium compounds. Specific examples of the magnesium compounds include, but are not limited to, magnesium halides such as magnesium chloride, magnesium bromide, magnesium iodide and magnesium fluoride; alkoxy magnesium halides such as methoxy magnesium chloride, ethoxy magnesium chloride, isopropoxy magnesium chloride, butoxy magnesium chloride and octoxy magnesium chloride; aryloxy magnesium halides such as phenoxy magnesium chloride and methylphenoxy magnesium chloride; alkoxy magnesiums such as ethoxy magnesium, isopropoxy magnesium, butoxy magnesium, n-octoxy magnesium and 2-ethylhexoxy magnesium; aryloxy magnesiums such as phenoxy magnesium and dimethylphenoxy magnesium; and carboxylic acid salts of magnesium such as magnesium laurate and magnesium stearate. These magnesium compounds may be in the liquid or solid state.

In one embodiment, the halogen containing magnesium compounds, such as magnesium chloride, alkoxy magnesium chlorides and aryloxy magnesium chlorides, are employed.

When preparing the solid catalyst component, an internal electron donor or a combination of internal electron donors can be added to the preparation and/or may form the solid catalyst component itself and/or other constituents. The solid titanium catalyst component can be made by contacting a magnesium compound and a titanium compound with an internal electron donor compound. In one embodiment, the solid titanium catalyst component is made by contacting a magnesium compound and a titanium compound in the presence of at least one internal electron donor compound. In another embodiment, the solid titanium catalyst component is made by forming a magnesium based support optionally with the titanium compound and optionally with at least one internal electron donor compound, and contacting the magnesium based support with the titanium compound and the at least one internal electron donor compound.

The catalyst prepared with two or several internal donors are different in comparison with the catalyst when the internal donors are used separately. In many cases the activities of catalysts with the two or several donors are higher in comparison with the catalyst having a single internal donor. The catalyst composition using at least two different donors provides a synergetic effect resulting in variable catalyst and polymer properties such as activities, isotactisity, molecular weight, and molecular weight distribution. It also results in reduction of the cost of producing the catalyst.

The internal electron donor compound comprises a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII):

wherein R₁ and R₂ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; and R₃, R₄, R₅, R₆, R₇, and R₈ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens.

As used herein, the term “cyclic” refers to a series of atoms connected to form a loop or ring. The term “cyclic” is meant to include monocyclic, bicyclic or polycyclic, alicyclic or aromatic, and/or homocyclic or heterocyclic compounds.

Examples of 1,8-naphthyl diester compound of the general formula (I) include, but are not limited to, naphthalene-1,8-diyl dibenzoate, 8-(benzoyloxy)naphthalen-1-yl 2-methylbenzoate, 8-(benzoyloxy)naphthalen-1-yl 3-methylbenzoate, 8-(benzoyloxy)naphthalen-1-yl 4-methylbenzoate, 8-(benzoyloxy)naphthalen-1-yl 2,4,6-trimethylbenzoate, 8-(benzoyloxy)naphthalen-1-yl isonicotinate, 8-(benzoyloxy)naphthalen-1-yl nicotinate, 8-(benzoyloxy)naphthalen-1-yl picolinate, 8-((cyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-((cyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-((2-methylcyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-((3-methylcyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-((4-methylcyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-(propionyloxy)naphthalen-1-yl benzoate, 8-(butyryloxy)naphthalen-1-yl benzoate, 8-(pentanoyloxy)naphthalen-1-yl benzoate, 8-(benzoyloxy)naphthalen-1-yl tetrahydro-2H-pyran-4-carboxylate, 8-(benzoyloxy)naphthalen-1-yl piperidine-4-carboxylate, and 8-(benzoyloxy)naphthalen-1-yl tetrahydro-2H-thiopyran-4-carboxylate.

In one embodiment, the secondary internal donor compound includes a compound represented by general formula (II):

wherein R₉ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₀ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; and R₁₁, R₁₂, R₁₃, R₁₄, R₁₅, and R₁₆ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens.

Examples of a compound represented by general formula (II) include, but are not limited to, 2-methoxy-1-naphthoic acid, methyl 2-methoxy-1-naphthoate, ethyl 2-methoxy-1-naphthoate, propyl 2-methoxy-1-naphthoate, butyl 2-methoxy-1-naphthoate, pentyl 2-methoxy-1-naphthoate, hexyl 2-methoxy-1-naphthoate, heptyl 2-methoxy-1-naphthoate, octyl 2-methoxy-1-naphthoate, nonyl 2-methoxy-1-naphthoate, undecyl 2-methoxy-1-naphthoate, dodecyl 2-methoxy-1-naphthoate, tridecyl 2-methoxy-1-naphthoate, tetradecyl 2-methoxy-1-naphthoate, pentadecyl 2-methoxy-1-naphthoate, hexadecyl 2-methoxy-1-naphthoate, heptadecyl 2-methoxy-1-naphthoate, heptadecyl 2-methoxy-1-naphthoate, octadecyl 2-methoxy-1-naphthoate, nonadecyl 2-methoxy-1-naphthoate, isopropyl 2-methoxy-1-naphthoate, isobutyl 2-methoxy-1-naphthoate, isopentyl 2-methoxy-1-naphthoate, 4-methylpentyl 2-methoxy-1-naphthoate, 5-methylhexyl 2-methoxy-1-naphthoate, 6-methylheptyl 2-methoxy-1-naphthoate, 7-methyloctyl 2-methoxy-1-naphthoate, 8-methylnonyl 2-methoxy-1-naphthoate, 9-methyldecyl 2-methoxy-1-naphthoate, 10-methylundecyl 2-methoxy-1-naphthoate, 11-methyldodecyl 2-methoxy-1-naphthoate, 12-methyltridecyl 2-methoxy-1-naphthoate, 13-methyltetradecyl 2-methoxy-1-naphthoate, 14-methylpentadecyl 2-methoxy-1-naphthoate, 15-methylhexadecyl 2-methoxy-1-naphthoate, 16-methylheptadecyl 2-methoxy-1-naphthoate, 17-methyloctadecyl 2-methoxy-1-naphthoate, and 18-methylnonadecyl 2-methoxy-1-naphthoate, methyl 2-ethoxy-1-naphthoate, methyl 2-propoxy-1-naphthoate, methyl 2-butoxy-1-naphthoate, methyl 2-(pentyloxy)-1-naphthoate, methyl 2-(hexyloxy)-1-naphthoate, methyl 2-(heptyloxy)-1-naphthoate, methyl 2-(octyloxy)-1-naphthoate, methyl 2-(decyloxy)-1-naphthoate, methyl 2-(undecyloxy)-1-naphthoate, methyl 2-(dodecyloxy)-1-naphthoate, methyl 2-(tridecyloxy)-1-naphthoate, methyl 2-(tetradecyloxy)-1-naphthoate, methyl 2-(pentadecyloxy)-1-naphthoate, methyl 2-(hexadecyloxy)-1-naphthoate, methyl 2-(heptadecyloxy)-1-naphthoate, methyl 2-isobutoxy-1-naphthoate, methyl 2-(isopentyloxy)-1-naphthoate, methyl 2-((4-methylpentyl)oxy)-1-naphthoate, methyl 2-((5-methylhexyl)oxy)-1-naphthoate, methyl 2-((6-methylheptyl)oxy)-1-naphthoate, methyl 2-((7-methyloctyl)oxy)-1-naphthoate, methyl 2-((9-methyldecyl)oxy)-1-naphthoate, methyl 2-((10-methylundecyl)oxy)-1-naphthoate, methyl 2-((11-methyldodecyl)oxy)-1-naphthoate, methyl 2-((12-methyltridecyl)oxy)-1-naphthoate, methyl 2-((13-methyltetradecyl)oxy)-1-naphthoate, methyl 2-((14-methylpentadecyl)oxy)-1-naphthoate, methyl 2-((15-methylhexadecyl)oxy)-1-naphthoate, methyl 2-((16-methylheptadecyl)oxy)-1-naphthoate, methyl 2-((16-methylheptadecyl)oxy)-1-naphthoate, methyl 2-((17-methyloctadecyl)oxy)-1-naphthoate, and methyl 2-((18-methylnonadecyl)oxy)-1-naphthoate.

In one embodiment, the secondary internal donor compound includes a compound represented by general formula (III):

wherein R₁₇ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₈ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; and R₁₉, R₂₀, R₂₁, and R₂₂ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens.

Examples of a compound represented by general formula (III) include, but are not limited to, butyl 2-methoxybenzoate, methyl 2-methoxybenzoate, ethyl 2-methoxybenzoate, propyl 2-methoxybenzoate, pentyl 2-methoxybenzoate, hexyl 2-methoxybenzoate, isopentyl 2-methoxybenzoate, isopropyl 2-methoxybenzoate, isobutyl 2-methoxybenzoate, 4-methylpentyl 2-methoxybenzoate, 5-methylhexyl 2-methoxybenzoate, undecyl 2-methoxybenzoate, tridecyl 2-methoxybenzoate, henicosyl 2-methoxybenzoate, 2-methoxybenzoic acid, butyl 2-hydroxybenzoate, butyl 2-ethoxybenzoate, butyl 2-propoxybenzoate, butyl 2-butoxybenzoate, butyl 2-methoxy-3-methylbenzoate, butyl 2-methoxy-4-methylbenzoate, butyl 2-methoxy-5-methylbenzoate, butyl 2-methoxy-6-methylbenzoate, butyl 3-chloro-2-methoxybenzoate, butyl 5-chloro-2-methoxybenzoate, butyl 4-chloro-2-methoxybenzoate, and butyl 2-chloro-6-methoxybenzoate.

In one embodiment, the secondary internal donor compound includes a compound represented by general formula (IV):

wherein R₂₃, R₂₄, and R₂₅ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens.

Examples of a compound represented by general formula (IV) include, but are not limited to, methyl 2,6-dimethoxybenzoate, ethyl 2,6-dimethoxybenzoate, propyl 2,6-dimethoxybenzoate, butyl 2,6-dimethoxybenzoate, pentyl 2,6-dimethoxybenzoate, hexyl 2,6-dimethoxybenzoate, heptyl 2,6-dimethoxybenzoate, octyl 2,6-dimethoxybenzoate, nonyl 2,6-dimethoxybenzoate, decyl 2,6-dimethoxybenzoate, dodecyl 2,6-dimethoxybenzoate, octadecyl 2,6-dimethoxybenzoate, phenyl 2,6-dimethoxybenzoate, cyclohexyl 2,6-dimethoxybenzoate, pyridin-4-yl 2,6-dimethoxybenzoate, tetrahydro-2H-pyran-4-yl 2,6-dimethoxybenzoate, isopropyl 2,6-dimethoxybenzoate, isobutyl 2,6-dimethoxybenzoate, isopentyl 2,6-dimethoxybenzoate, 4-methylpentyl 2,6-dimethoxybenzoate, 5-methylhexyl 2,6-dimethoxybenzoate, 6-methylheptyl 2,6-dimethoxybenzoate, 7-methyloctyl 2,6-dimethoxybenzoate, 8-methylnonyl 2,6-dimethoxybenzoate, 9-methyldecyl 2,6-dimethoxybenzoate, butyl 2-ethoxy-6-methoxybenzoate, butyl 2-methoxy-6-propoxybenzoate, 7-methyloctyl 2-ethoxy-6-methoxybenzoate, and 7-methyloctyl 2-methoxy-6-propoxybenzoate.

In one embodiment, the secondary internal donor compound includes a compound represented by general formula (V):

wherein R₂₆ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₂₇, R₂₈, R₂₉, and R₃₀ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; and R₃₁, R₃₂, R₃₃, R₃₄, R₃₅, R₃₆, R₃₇, and R₃₈ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens.

Examples of a compound represented by general formula (V) include, but are not limited to, (2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (2-ethoxyphenyl)(pyrrolidin-1-yl)methanone, (2-propoxyphenyl)(pyrrolidin-1-yl)methanone, (2-butoxyphenyl)(pyrrolidin-1-yl)methanone, (2-(pentyloxy)phenyl)(pyrrolidin-1-yl)methanone, (2-(hexyloxy)phenyl)(pyrrolidin-1-yl)methanone, (2-(dodecyloxy)phenyl)(pyrrolidin-1-yl)methanone, (2-(icosyloxy)phenyl)(pyrrolidin-1-yl)methanone, (2-isopropoxyphenyl)(pyrrolidin-1-yl)methanone, (2-isobutoxyphenyl)(pyrrolidin-1-yl)methanone, (2-(isopentyloxy)phenyl)(pyrrolidin-1-yl)methanone, (2-phenoxyphenyl)(pyrrolidin-1-yl)methanone, (2-(cyclohexyloxy)phenyl)(pyrrolidin-1-yl)methanone, (2-(pyridin-4-yloxy)phenyl)(pyrrolidin-1-yl)methanone, pyrrolidin-1-yl(2-((tetrahydro-2H-pyran-4-yl)oxy)phenyl)methanone, (2-(2-ethoxyethoxy)phenyl)(pyrrolidin-1-yl)methanone, (2-(2-(ethylamino)ethoxy)phenyl)(pyrrolidin-1-yl)methanone, (2-methoxyphenyl)(2-methylpyrrolidin-1-yl)methanone, (2-chloropyrrolidin-1-yl)(2-methoxyphenyl)methanone, (2-methoxyphenyl)(3-methylpyrrolidin-1-yl)methanone, (3-chloropyrrolidin-1-yl)(2-methoxyphenyl)methanone, (2-methoxy-5-methylphenyl)(pyrrolidin-1-yl)methanone, (2-methoxy-3-methylphenyl)(pyrrolidin-1-yl)methanone, (2-methoxy-4-methylphenyl)(pyrrolidin-1-yl)methanone, (2-methoxy-6-methylphenyl)(pyrrolidin-1-yl)methanone, (5-bromo-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (3-bromo-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (4-bromo-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (2-bromo-6-methoxyphenyl)(pyrrolidin-1-yl)methanone, (5-chloro-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (3-chloro-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (4-chloro-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (2-chloro-6-methoxyphenyl)(pyrrolidin-1-yl)methanone, (5-fluoro-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (3-fluoro-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (4-fluoro-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (2-fluoro-6-methoxyphenyl)(pyrrolidin-1-yl)methanone, (5-iodo-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (3-iodo-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (4-iodo-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, and (2-iodo-6-methoxyphenyl)(pyrrolidin-1-yl)methanone.

In one embodiment, the secondary internal donor compound includes a compound represented by general formula (VI):

wherein R₃₉ and R₄₀ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens.

Examples of a compound represented by general formula (VI) include, but are not limited to, dibutyl phthalate (DnBP), diisobutyl phthalate (DIBP), dioctyl phthalate (DOP), bis(2-ethylhexyl) phthalate (DEHP), bis(6-methylheptyl) phthalate (DiOP, aka diisooctyl phthalate), bis(7-methyloctyl) phthalate (DINP), and bis(2-propylheptyl) phthalate (DPHP).

In one embodiment, the secondary internal donor compound includes a compound represented by general formula (VII):

wherein R₄₁ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; and R₄₂ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens.

Examples of a compound represented by general formula (VII) include, but are not limited to, methyl acetate, ethyl acetate, propyl acetate, butyl acetate, pentyl acetate, hexyl acetate, heptyl acetate, octyl acetate, phenyl acetate, cyclohexyl acetate, isobutyl acetate, isopentyl acetate, 4-methylpentyl acetate, 5-methylhexyl acetate, 6-methylheptyl acetate, 7-methyloctyl acetate, methyl propionate, methyl butyrate, methyl pentanoate, methyl hexanoate, methyl heptanoate, methyl octanoate, methyl decanoate, methyl dodecanoate, methyl stearate, methyl benzoate, methyl cyclohexanecarboxylate, methyl 3-methylbutanoate, methyl 4-methylpentanoate, methyl 5-methylhexanoate, methyl 6-methylheptanoate, methyl 7-methyloctanoate, methyl 9-methyldecanoate, methyl 11-methyldodecanoate, and methyl 16-methylheptadecanoate.

In one embodiment, the secondary internal donor compound includes a compound represented by general formula (VIII):

wherein R₄₃ and R₄₄ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens.

Examples of a compound represented by general formula (VIII) include, but are not limited to, dibutyl cyclohexane-1,2-dicarboxylate, diisobutyl cyclohexane-1,2-dicarboxylate, dioctyl cyclohexane-1,2-dicarboxylate, bis(2-ethylhexyl)cyclohexane-1,2-dicarboxylate, bis(6-methylheptyl)cyclohexane-1,2-dicarboxylate, bis(7-methyloctyl)cyclohexane-1,2-dicarboxylate, and bis(2-propylheptyl)cyclohexane-1,2-dicarboxylate.

In one embodiment, the solid catalyst component comprises an internal electron donor compound containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII), but does not include additional internal electron donors. In another embodiment, the solid catalyst component includes other internal electron donors in addition to the internal electron donor compound containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII). For example, when preparing the solid catalyst component, other internal electron donors can be added to the preparation and/or may form the solid catalyst itself and/or other constituents in addition to the internal electron donor containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII).

Examples of other internal electron donors include oxygen-containing electron donors such as organic acid esters. Specific examples include, but are not limited to, diethyl ethylmalonate, diethyl propylmalonate, diethyl isopropylmalonate, diethyl butylmalonate, diethyl 1,2-cyclohexanedicarboxylate, di-2-ethylhexyl 1,2-cyclohexanedicarboxylate, di-2-isononyl 1,2-cyclohexanedicarboxylate, methyl benzoate, ethyl benzoate, propyl benzoate, butyl benzoate, octyl benzoate, cyclohexyl benzoate, phenyl benzoate, benzyl benzoate, methyl 4-methylbenzoate, ethyl 4-methylbenzoate, amyl 4-methylbenzoate, ethyl 4-ethylbenzoate, methyl anisate, ethyl anisate, ethyl 4-ethoxybenzoate, diisononyl phthalate, di-2-ethylhexyl phthalate, diethyl succinate, dipropyl succinate, diisopropyl succinate, dibutyl succinate, diisobutyl succinate, dioctyl succinate, diisononyl succinate, and diether compounds such as 9,9-bis(methoxymethyl)fluorine, 2-isopropyl-2-isopentyl-1,3-dimethoxypropane, 2,2-diisobutyl-1,3-dimethoxypropane, 2,2-diisopentyl-1,3-dimethoxypropane, and 2-isopropyl-2-cyclohexyl-1,3-dimethoxypropane.

The internal electron donor compounds may be added individually or together. In employing the internal electron donor compounds, they do not have to be used directly as starting materials, but compounds convertible to the electron donors in the course of preparing the solid catalyst components may also be used as the starting materials.

The solid catalyst component can be made by contacting a magnesium compound and a titanium compound with an internal electron donor compound containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII).

In one embodiment, the solid catalyst component is made by contacting a magnesium compound and a titanium compound in the presence of an internal electron donor compound containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII). In another embodiment, the solid catalyst component is made by forming a magnesium based support optionally with a titanium compound and optionally with an internal electron donor compound containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII), and contacting the magnesium based support with the titanium compound and the internal electron donor compound containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII). In yet another embodiment, the solid catalyst component is made by contacting a magnesium based support with a titanium compound to form a mixture, then contacting the mixture with an internal electron donor compound containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII). In still yet another embodiment, the solid catalyst component is made by contacting a magnesium based support with a titanium compound to form a mixture, then contacting the mixture with an internal electron compound containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII), then contacting the mixture again with the internal electron donor compound containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII). Such repeated contact with the internal electron donor compound containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII), can occur once, twice, or three times successively or with other acts performed between contacts with additional doses of the internal electron donor compounds containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII).

Generally, the magnesium based support is made by dissolving a magnesium compound in a solvent mixture comprising an organic epoxy compound, an organic phosphorus compound and an optional inert diluent to form a homogenous solution.

The organic epoxy compounds used can include compounds having at least one epoxy group in the forms of monomers, dimmers, oligomers and polymers. Examples of epoxy compounds include, but are not limited to, aliphatic epoxy compounds, alicyclic epoxy compounds, aromatic epoxy compounds, or the like. Examples of aliphatic epoxy compounds include, but are not limited to, halogenated aliphatic epoxy compounds, aliphatic epoxy compounds having a keto group, aliphatic epoxy compounds having an ether bond, aliphatic epoxy compounds having an ester bond, aliphatic epoxy compounds having a tertiary amino group, aliphatic epoxy compounds having a cyano group, or the like. Examples of alicyclic epoxy compounds include, but are not limited to halogenated alicyclic epoxy compounds, alicyclic epoxy compounds having a keto group, alicyclic epoxy compounds having an ether bond, alicyclic epoxy compounds having an ester bond, alicyclic epoxy compounds having a tertiary amino group, alicyclic epoxy compounds having a cyano group, or the like. Examples of aromatic epoxy compounds include, but are not limited to, halogenated aromatic epoxy compounds, aromatic epoxy compounds having a keto group, aromatic epoxy compounds having an ether bond, aromatic epoxy compounds having an ester bond, aromatic epoxy compounds having a tertiary amino group, aromatic epoxy compounds having a cyano group, or the like.

Specific examples of epoxy compounds include, but are not limited to, epifluorohydrin, epichlorohydrin, epibromohydrin, hexafluoropropylene oxide, 1,2-epoxy-4-fluorobutane, 1-(2,3-epoxypropyl)-4-fluorobenzene, 1-(3,5-epoxybutyl)-2-fluorobenzene, 1-(2,3-epoxypropyl)-4-chlorobenzene, 1-(3,5-epoxybutyl)-3-chlorobenzene, or the like. Specific examples of halogenated alicyclic epoxy compounds include 4-fluoro-1,2-cyclohexene oxide, 6-chloro-2,3 epoxybicyclo[2,2,1]heptane, or the like. Specific examples of halogenated aromatic epoxy compounds include 4-fluorostyrene oxide, 1-(1,2-epoxypropyl)-3-trifluorobenzene, or the like.

The organic phosphorus compounds can include, but are not limited, to hydrocarbyl esters and halohydrocarbyl esters of ortho-phosphoric acid and phosphorous acid. Specific examples include, but are not limited to trimethyl phosphate, triethyl phosphate, tributyl phosphate, triphenyl phosphate, trimethyl phosphite, triethyl phosphite, tributyl phosphite and triphenyl phosphite.

In order to improve the ability of the magnesium compound to be dissolved, an inert diluent may be optionally added to the solvent mixture. The inert diluent can typically be aromatic hydrocarbons or alkanes, as long as it is capable of facilitating the dissolution of the magnesium compound. Examples of aromatic hydrocarbons include, but are not limited to benzene, toluene, xylene, chlorobenzene, dichlorobenzene, trichlorobenzene, chlorotoluene, and derivatives thereof. Examples of alkanes include linear, branched, or cyclic alkanes having about 3 to about 30 carbons, such as butane, pentane, hexane, cyclohexane, heptanes, and the like. These inert diluents may be used alone or in combination.

In embodiments of preparing the solid catalyst component according to the Examples, the magnesium based support is mixed with a titanium compound such as liquid titanium tetrahalide to form a solid precipitate in the optional presence of an auxiliary precipitant. The auxiliary precipitant may be added before, during or after the precipitation of the solids and loaded on the solids.

The auxiliary precipitants used can include carboxylic acids, carboxylic acid anhydrides, ethers, ketones, or mixture thereof. Specific examples include, but are not limited to, acetic anhydride, phthalic anhydride, succinic anhydride, maleic anhydride, 1,2,4,5-benzene tetracarboxylic dianhydride, acetic acid, propionic acid, butyric acid, acrylic acid, methacrylic acid, acetone, methyl ethyl ketone, benzophenone, dimethyl ether, diethyl ether, dipropyl ether, dibutyl ether, and dipentyl ether.

Solid precipitation can be carried out by one or more processes selected from the following. One method involves mixing a titanium compound such as liquid titanium tetrahalide with a magnesium based support at a temperature in the range of about −40 degrees Celsius to about 0 degrees Celsius, and precipitating the solids while the temperature is raised slowly to a range from about 30 degrees Celsius to about 120 degrees Celsius, for example from about 60 degrees Celsius to about 100 degrees Celsius, but not by way of limitation. The second method involves adding a titanium compound dropwise into a magnesium based support to precipitate out solids immediately. The third method involves adding a first titanium compound dropwise into a magnesium based support and mixing a second titanium compound with the magnesium based support. In these methods, an internal electron donor compound containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII) can be present in the reaction system. The internal electron donor compound containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII) can be added either after the magnesium based support is obtained or after the solid precipitate is formed.

In one embodiment, when the solid catalyst component is formed, a surfactant can be used so as to produce a relatively large size and substantially spherical shape of the magnesium based support, thereby contributing to many of the beneficial properties of the solid catalyst component and catalyst system. General examples of surfactants include polymer surfactants, such as polyacrylates, polymethacrylates, polyalkyl methacrylates, and the like. A polyalkyl methacrylate is a polymer that may contain one or more methacrylate monomers, such as at least two different methacrylate monomers, at least three different methacrylate monomers, etc. Moreover, the acrylate and methacrylate polymers may contain monomers other than acrylate and methacrylate monomers, so long as the polymer surfactant contains at least about 40% by weight acrylate and methacrylate monomers.

In one embodiment, non-ionic surfactants and/or anionic surfactants can be used. Examples of non-ionic surfactants and/or anionic surfactants include, but are not limited to, phosphate esters, alkyl sulfonates, aryl sulfonates, alkylaryl sulfonates, linear alkyl benzene sulfonates, alkylphenols, ethoxylated alcohols, carboxylic esters, fatty alcohols, fatty esters, fatty aldehydes, fatty ketones, fatty acid nitriles, benzene, naphthalene, anthracene, succinic anhydride, phthalic anhydrides, rosin, terpene, phenol, or the like. In fact, a number of anhydride surfactants are effective. In some instances, the absence of an anhydride surfactant causes the formation of very small catalyst support particles while the over-use creates straw shaped material sometimes referred to as needles.

The solid catalyst precursor can be formed in one embodiment as follows. In a solvent such as toluene, a magnesium and titanium containing solution is seen following the addition of a halogenating agent such as TiCl₄ into a magnesium based solution at relatively cooler temperatures, such as −25 degrees Celsius until about 0 degrees Celsius. An oil phase is then formed, which can be dispersed into the hydrocarbon phase that is stable until about 40 degrees Celsius. The resultant magnesium material becomes a semi-solid at this point and the particle morphology is thereafter determined. The semi-solid product converts into a solid between about 40 degrees Celsius and about 80 degrees Celsius.

In order to facilitate obtaining uniform solid particles, the process of precipitation can be carried out slowly. When the second method of adding titanium halide dropwise at low or room temperature is applied, the process may take place over a period from about 1 hour to about 6 hours. When the first method of raising the temperature in a slow manner is applied as described hereinafter, the rate of temperature increase can range from about 4 degrees Celsius to about 125 degrees Celsius per hour.

The solid precipitate is first separated from the mixture. Entrained in the solid precipitate may be a variety of complexes and byproducts, so that further treatment may in some instances be necessary as would be well appreciated and understood by one of ordinary skill in the art. In one embodiment, the solid precipitate is treated with a titanium compound in order to substantially remove the byproducts from the solid precipitate.

The solid precipitate can be washed with an inert diluent and then treated with a titanium compound or a mixture of a titanium compound and an inert diluent. The titanium compound used in this treatment can be identical to or different than the titanium compound used for forming the solid precipitate. The amount of titanium compound used is from about 1 to about 20 moles, such as from about 2 to about 15 moles, per mole of magnesium compound in the support. The treatment temperature ranges from about 50 degrees Celsius to about 150 degrees Celsius, such as from about 60 degrees Celsius to about 100 degrees Celsius. If a mixture of titanium tetrahalide and an inert diluent is used to treat the solid precipitate, the volume % of titanium tetrahalide in the treating solution is from about 10% to about 100%, the rest being the inert diluent.

The treated solids can be further washed with an inert diluent to remove ineffective titanium compounds and other byproducts. The inert diluent herein used can be hexane, heptanes, octane, 1,2-dichloroethane, benzene, toluene, ethylbenzene, xylene, and other hydrocarbons.

By treating the solid precipitate with the titanium compound and optionally an inert diluent, the byproducts in the solid precipitate can be removed from the solid precipitate. In one embodiment, the solid precipitate is treated with the titanium compound and optionally an inert diluent about two times or more and five times or less.

By treating the solid precipitate with an inert diluent, a free titanium compound in the solid precipitate can be removed from the solid precipitate. The resultant solid precipitate does not, in such circumstances, substantially contain a free titanium compound. In one embodiment, the solid precipitate is treated repeatedly with an inert diluent until the filtrate contains about 100 ppm or less of titanium. In another embodiment, the solid precipitate is treated repeatedly with an inert diluent until the filtrate contains about 50 ppm or less of titanium. In yet another embodiment, the solid precipitate is treated with an inert diluent until the filtrate contains about 10 ppm or less of titanium. In one embodiment, the solid precipitate is treated with an inert diluent about three times or more and seven times or less. In all cases, one of ordinary skill in the art, given the present disclosure, would be able to vary these parameters and steps in order to tailor to specific conditions and/or properties as described.

In one embodiment, the solid catalyst component contains from about 0.5 to about 6.0 wt % titanium; from about 10 to about 25 wt % magnesium; from about 40 to about 70 wt % halogen; from about 1 to about 50 wt % the internal electron donor compound containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII); and optionally inert diluent from about 0 to about 15 wt %. In another embodiment, the solid catalyst component contains from about 2 to about 25 wt % of one or more of the internal electron donors containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII). In yet another embodiment, the solid catalyst component contains from about 5 to about 20 wt % of one or more of the internal electron donors containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII).

The amounts of the ingredients used in preparing the solid catalyst component may vary depending upon the method of preparation. In one embodiment, from about 0.01 to about 5 moles of the internal electron donor compounds containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII) and from about 0.01 to about 500 moles of the titanium compounds are used per mole of the magnesium compound used to make the solid catalyst component. In another embodiment, from about 0.05 to about 2 moles of the internal electron donor compounds containing a combination of internal electron donor compounds comprising at least one 1,8-naphthyl diester compound represented by general formula (I) and at least one secondary internal donor compound selected from the group consisting of a compound represented by general formula (II), (III), (IV), (V), (VI), (VII), and (VIII) and from about 0.05 to about 300 moles of the titanium compounds are used per mole of the magnesium compound used to make the solid catalyst component.

In one embodiment, in the solid catalyst component, the atomic ratio of halogen/titanium is from about 4 to about 200; the internal electron donor/titanium mole ratio is from about 0.01 to about 10; and the magnesium/titanium atomic ratio is from about 1 to about 100. In another embodiment, in the solid catalyst component, the atomic ratio of halogen/titanium is from about 5 to about 100; the internal electron donor/titanium mole ratio is from about 0.2 to about 6; and the magnesium/titanium atomic ratio is from about 2 to about 50.

The resulting solid catalyst component generally contains a magnesium halide of a smaller crystal size than traditional and/or commercially available magnesium halides and usually has a specific surface area of at least about 5 m²/g, such as from about 10 to about 1,000 m²/g or from about 100 to about 800 m²/g. Since the above ingredients are unified to form an integral structure of the solid catalyst component, the composition of the solid catalyst component does not substantially change by washing with, for example, hexane.

The solid catalyst component may be used after being diluted with an inorganic or organic compound such as a silicon compound, an aluminum compound, or the like. One of ordinary skill in the art would appreciate that while such dilution may be desirable in certain situations it is not necessary for all applications.

Methods of preparing solid catalyst components, which can be used in the presently disclosed and claimed inventive concept(s), are described in U.S. patents and U.S. patent Publication Nos: U.S. Pat. Nos. 4,771,023; 4,784,983; 4,829,038; 4,861,847; 4,990,479; 5,177,043; 5,194,531; 5,244,989; 5,438,110; 5,489,634; 5,576,259; 5,767,215; 5,773,537; 5,905,050; 6,323,152; 6,437,061; 6,469,112; 6,962,889; 7,135,531; 7,153,803; 7,271,119; 2004242406; 20040242407; and 20070021573 which are hereby incorporated by reference in their entirety as those set forth explicitly therein in this regard.

The catalyst system may contain at least one organoaluminum compound in addition to the solid catalyst component. Compounds having at least one aluminum-carbon bond in the molecule can be used as the organoaluminum compound. Examples of organoaluminum compounds include compounds of the following chemical formula (2):

AlR_(n)X_(3-n)  (2)

In chemical formula (3), R independently represents a hydrocarbon group usually having 1 to about 20 carbon atoms, X represents a halogen atom(s), and 0<n≦3.

Specific examples of the organoaluminum compounds represented by chemical formula (3) include, but are not limited to, trialkyl aluminums such as triethyl aluminum, tributyl aluminum and trihexyl aluminum; trialkenyl aluminums such as triisoprenyl aluminum; dialkyl aluminum halides such as diethyl aluminum chloride, dibutyl aluminum chloride and diethyl aluminum bromide; alkyl aluminum sesquihalides such as ethyl aluminum sesquichloride, butyl aluminum sesquichloride and ethyl aluminum sesquibromide; alkyl aluminum dihalides such as ethyl aluminum dichloride, propyl aluminum dichloride and butyl aluminum dibromide; dialkyl aluminum hydrides such as diethyl aluminum hydride and dibutyl aluminum hydride; and other partially hydrogenated alkyl aluminum such as ethyl aluminum dihydride and propyl aluminum dihydride.

The organoaluminum compound can be used in the catalyst system in an amount that the mole ratio of aluminum to titanium (from the solid catalyst component) is from about 5 to about 1,000. In another embodiment, the mole ratio of aluminum to titanium in the catalyst system is from about 10 to about 700. In yet another embodiment, the mole ratio of aluminum to titanium in the catalyst system is from about 25 to about 400.

The catalyst system may contain at least one organosilicon compound in addition to the solid catalyst component. This organosilicon compound may, although not always, be referred as an external electron donor. The organosilicon compound contains silicon having at least one hydrogen ligand (hydrocarbon group). General examples of hydrocarbon groups include alkyl groups, cycloalkyl groups, (cycloalkyl)methylene groups, alkene groups, aromatic groups, and the like.

The organosilicon compound, when used as an external electron donor serving as one component of a Ziegler-Natta catalyst system for olefin polymerization, improves the ability of the catalyst system to produce a polymer (at least a portion of which is polyolefin) having a controllable crystallinity while retaining high performance with respect to catalytic activity.

The organosilicon compound is used in the catalyst system in an amount that the mole ratio of the organoaluminum compound to the organosilicon compound is from about 2 to about 90. In another embodiment, the mole ratio of the organoaluminum compound to the organosilicon compound is from about 5 to about 70. In yet another embodiment, the mole ratio of the organoaluminum compound to the organosilicon compound is from about 7 to about 35.

In one embodiment, the organosilicon compound is represented by chemical formula (4):

R_(n)Si(OR′)_(4-n)  (4)

wherein each R and R′ independently represent a hydrocarbon group, and n is 0≦n<4.

Specific examples of the organosilicon compound of chemical formula (4) include, but are not limited to, trimethylmethoxysilane, trimethylethoxysilane, dimethyldimethoxysilane, dimethyldiethoxysilane, diisopropyldimethoxysilane, diisobutyldimethoxysilane, t-butylmethyldimethoxysilane, t-butylmethyldiethoxysilane, t-amylmethyldiethoxysilane, dicyclopentyldimethoxysilane, diphenyldimethoxysilane, phenylmethyldimethoxysilane, diphenyldiethoxysilane, bis-o-tolydimethoxysilane, bis-m-tolydimethoxysilane, bis-p-tolydimethoxysilane, bis-p-tolydiethoxysilane, bisethylphenyldimethoxysilane, dicyclohexyldimethoxysilane, cyclohexylmethyldimethoxysilane, cyclohexylmethyldiethoxysilane, ethyltrimethoxysilane, ethyltriethoxysilane, vinyltrimethoxysilane, methyltrimethoxysilane, n-propyltriethoxysilane, decyltrimethoxysilane, decyltriethoxysilane, phenyltrimethoxysilane, gamma-chloropropyltrimethoxysilane, methyltriethoxysilane, ethyltriethoxysilane, vinyltriethoxysilane, t-butyltriethoxysilane, n-butyltriethoxysilane, iso-butyltriethoxysilane, phenyltriethoxysilane, gamma-amniopropyltriethoxysilane, cholotriethoxysilane, ethyltriisopropoxysi lane, vinyltirbutoxysilane, cyclohexyltrimethoxysilane, cyclohexyltriethoxysilane, 2-norbornanetrimethoxysilane, 2-norbornanetriethoxysilane, 2-norbornanemethyldimethoxysilane, ethyl silicate, butyl silicate, trimethylphenoxysilane, and methyltriallyloxysilane.

In another embodiment, the organosilicon compound is represented by chemical formula (5):

SiRR′_(m)(OR″)_(3-m)  (5)

wherein 0≦m<3, such as 0≦m≦2; and R independently represents a cyclic hydrocarbon or substituted cyclic hydrocarbon group. Specific examples of the group R include, but are not limited to, cyclopropyl; cyclobutyl; cyclopentyl; 2-methylcyclopentyl; 3-methylcyclopentyl; 2-ethylcyclopentyl; 3-propylcyclopentyl; 3-isopropylcyclopentyl; 3-butylcyclopentyl; 3-tertiary butyl cyclopentyl; 2,2-dimethylcyclopentyl; 2,3-dimethylcyclopentyl; 2,5-dimethylcyclopentyl; 2,2,5-trimethylcyclopentyl; 2,3,4,5-tetramethylcyclopentyl; 2,2,5,5-tetramethylcyclopentyl; 1-cyclopentylpropyl; 1-methyl-1-cyclopentylethyl; cyclopentenyl; 2-cyclopentenyl; 3-cyclopentenyl; 2-methyl-1-cyclopentenyl; 2-methyl-3-cyclopentenyl; 3-methyl-3-cyclopentenyl; 2-ethyl-3-cyclopentenyl; 2,2-dimethyl-3-cyclopentenyl; 2,5-dimethyl-3-cyclopentenyl; 2,3,4,5-tetramethyl-3-cyclopentenyl; 2,2,5,5-tetramethyl-3-cyclopentenyl; 1,3-cyclopentadienyl; 2,4-cyclopentadienyl; 1,4-cyclopentadienyl; 2-methyl-1,3-cyclopentadienyl; 2-methyl-2,4-cyclopentadienyl; 3-methyl-2,4-cyclopentadienyl; 2-ethyl-2,4-cyclopentadienyl; 2,2-dimethyl-2,4-cyclopentadienyl; 2,3-dimethyl-2,4-cyclopentadienyl; 2,5-dimethyl-2,4-cyclopentadienyl; 2,3,4,5-tetramethyl-2,4-cyclopentadienyl; indenyl; 2-methylindenyl; 2-ethylindenyl; 2-indenyl; 1-methyl-2-indenyl; 1,3-dimethyl-2-indenyl; indanyl; 2-methylindanyl; 2-indanyl; 1,3-dimethyl-2-indanyl; 4,5,6,7-tetrahydroindenyl; 4,5,6,7-tetrahydro-2-indenyl; 4,5,6,7-tetrahydro-1-methyl-2-indenyl; 4,5,6,7-tetrahydro-1,3-dimethyl-2-indenyl; fluorenyl groups; cyclohexyl; methylcyclohexyls; ethylcyclohexyls; propylcyclohexyls; isopropylcyclohexyls; n-butylcyclohexyls; tertiary-butyl cyclohexyls; dimethylcyclohexyls; and trimethylcyclohexyls.

In chemical formula (5), R′ and R″ are identical or different and each represents a hydrocarbon. Examples of R′ and R″ are alkyl, cycloalkyl, aryl and aralkyl groups having 3 or more carbon atoms. Furthermore, R and R′ may be bridged by an alkyl group, etc. General examples of organosilicon compounds are those of chemical formula (5) in which R is cyclopentyl group, R′ is an alkyl group such as methyl or cyclopentyl group, and R″ is an alkyl group, particularly a methyl or ethyl group.

Specific examples of organosilicon compound of chemical formula (5) include, but are not limited to, trialkoxysilanes such as cyclopropyltrimethoxysilane, cyclobutyltrimethoxysilane, cyclopentyltrimethoxysilane, 2-methylcyclopentyltrimethoxysane, 2,3-dimethylcyclopentyltrimethoxysilane, 2,5-dimethylcyclopentyltrimethoxysilane, cyclopentyltriethoxysilane, cyclopentenyltrimethoxysilane, 3-cyclopentenyltrimethoxysilane, 2,4-cyclopentadienyltrimethoxysilane, indenyltrimethoxysilane and fluorenyltrimethoxysilane; dialkoxysilanes such as dicyclopentyldimethoxysilane, bis(2-methylcyclopentyl)dimethoxysilane, bis(3-tertiary butylcyclopentyl)dimethoxysilane, bis(2,3-dimethylcyclopentyl)dimethoxysilane, bis(2,5-dimethylcyclopentyl)dimethoxysilane, dicyclopentyldiethoxysilane, dicyclobutyldiethoxysilane, cyclopropylcyclobutyldiethoxysilane, dicyclopentenyldimethoxysilane, di(3-cyclopentenyl)dimethoxysilane, bis(2,5-dimethyl-3-cyclopentenyl)dimethoxysilane, di-2,4-cyclopentadienyl)dimethoxysilane, bis(2,5-dimethyl-2,4-cyclopentadienyl)dimethoxysilane, bis(1-methyl-1-cyclopentylethyl)dimethoxysilane, cyclopentylcyclopentenyldimethoxysilane, cyclopentylcyclopentadienyldimethoxysilane, diindenyldimethoxysilane, bis(1,3-dimethyl-2-indenyl)dimethoxysilane, cyclopentadienylindenyldimethoxysilane, difluorenyldimethoxysilane, cyclopentylfluorenyldimethoxysilane and indenylfluorenyldimethoxysilane; monoalkoxysilanes such as tricyclopentylmethoxysilane, tricyclopentenylmethoxysilane, tricyclopentadienylmethoxysilane, tricyclopentylethoxysilane, dicyclopentylmethylmethoxysilane, dicyclopentylethylmethoxysilane, dicyclopentylmethylethoxysilane, cyclopentyldimethylmethoxysilane, cyclopentyldiethylmethoxysilane, cyclopentyldimethylethoxysilane, bis(2,5-dimethylcyclopentyl)cyclopentylmethoxysilane, dicyclopentylcyclopentenylmethoxysilane, dicyclopentylcyclopentenadienylmethoxysilane and diindenylcyclopentylmethoxysilane; and ethylenebis-cyclopentyldimethoxysilane.

Polymerization of olefins is carried out in the presence of the catalyst system described above. Generally, olefins are contacted with the catalyst system described above under suitable conditions to form desired polymer products. In one embodiment, preliminary polymerization described below is carried out before main polymerization. In another embodiment, polymerization is carried out without preliminary polymerization. In yet another embodiment, the formation of copolymer is carried out using at least two polymerization zones.

In preliminary polymerization, the solid catalyst component is usually employed in combination with at least a portion of the organoaluminum compound. This process may be carried our partially or completely in the presence of the organosilicon compound (i.e. the external electron donor compound). The concentration of the catalyst system used in the preliminary polymerization reactor may be much higher than that in the reaction system of the main polymerization.

The concentration of the solid catalyst component in the preliminary polymerization reactor is usually from about 0.01 to about 200 millimoles, including from about 0.05 to about 100 millimoles, calculated as titanium atoms per liter of an inert hydrocarbon medium described below. In one embodiment, the preliminary polymerization is carried out by adding an olefin and the above catalyst system ingredients to an inert hydrocarbon medium and polymerizing the olefin under controllable conditions.

Specific examples of the inert hydrocarbon medium include, but are not limited to, aliphatic hydrocarbons such as propane, butane, pentane, hexane, heptanes, octane, decane, dodecane and kerosene; alicyclic hydrocarbons such as cyclopentane, cyclohexane and methylcyclopentane; and aromatic hydrocarbons such as benzene, toluene and xylene; and mixtures thereof. In a certain embodiment, a liquid olefin may be used partially or completely as the inert hydrocarbon medium.

The reaction temperature for the preliminary polymerization is sufficient for the resulting preliminary polymer to be substantially insoluble in the inert hydrocarbon medium. In one embodiment, the temperature is from about −20 degrees Celsius to about 100 degrees Celsius. In another embodiment, the temperature is from about −10 degrees Celsius to about 80 degrees Celsius. In yet another embodiment, the temperature is from about 0 degrees Celsius to about 40 degrees Celsius.

Optionally, a molecular-weight controlling agent, such as hydrogen, may be used in the preliminary polymerization. The molecular weight controlling agent is used in such an amount that the polymer obtained by the preliminary polymerization has an intrinsic viscosity, measured in decalin at 135 degrees Celsius, of at least about 0.2 dl/g, and including from about 0.5 to 10 dl/g.

In one embodiment, the preliminary polymerization is desirably carried out so that from about 0.1 g to about 1,000 g of a polymer is formed per gram of the solid catalyst component of the catalyst system. In another embodiment, the preliminary polymerization is desirably carried out so that from about 0.3 g to about 500 g of a polymer is formed per gram of the solid catalyst component. If the amount of the polymer formed by the preliminary polymerization is too large, the efficiency of producing the olefin polymer in the main polymerization may sometimes decrease, and when the resulting olefin polymer is molded into a film or another article, “fish eyes” (i.e. granular dots or small circles in a molded article of otherwise uniform and constant transparency) tend to occur in the molded article. The preliminary polymerization may be carried out batchwise or continuously.

After the preliminary polymerization is conducted as outlined above, or alternatively, without performing the preliminary polymerization, the main polymerization of an olefin feedstock is carried out in the presence of the above-described olefin polymerization catalyst system, i.e. the catalyst system is formed from the solid catalyst component, the organoaluminum compound and the organosilicon compound (the external electron donor compound).

Examples of olefins that can be used in the main polymerization are alpha-olefins having 2 to 20 carbon atoms such as ethylene, propylene, 1-butene, 4-methyl-1-pentene, 1-pentene, 1-octene, 1-hexene, 1-methyl-1-pentene, 3-methyl-1-pentene, 3-methyl-1-butene, 1-decene, 1-tetradecene, 1-eicosene, and vinylcyclohexane. In the process of the presently disclosed and claimed inventive concept(s), these alpha-olefins may be used individually or in any combinations as will be apparent to one of ordinary skill in the art given the present disclosure.

In one embodiment, propylene or 1-butene is homopolymerized, or, alternatively, a mixed olefin containing propylene or 1-butene as a main component is copolymerized. When a mixed olefin is selected or used, the proportion of propylene or 1-butene as the main component is usually at least about 50 mole %, including at least about 70 mole %.

By performing the preliminary polymerization, the catalyst system thereafter utilized in the main polymerization can be adjusted to select different degrees of activity. This adjustment tends to result in a powdery polymer having a high bulk density. Furthermore, when the preliminary polymerization is carried out, the particle shape of the resulting polymer becomes spherical. In the case of slurry polymerization, the slurry attains excellent characteristics, while in the case of gas phase polymerization, the polymer seed bed attains excellent characteristics. Each type of polymerization is preceded by the preliminary polymerization as described herein. Furthermore, in these embodiments, a polymer having a high stereoregularity index can be produced with a high catalytic efficiency by polymerizing an alpha-olefin having at least 3 carbon atoms. Accordingly, when producing the propylene copolymer, the resulting copolymer powder or the copolymer becomes easy to process.

In the homopolymerization of these olefins, a polyunsaturated compound such as conjugated diene or non-conjugated diene may be used as a comonomer. Examples of co-monomers include styrene, butadiene, acrylonitrile, acrylamide, alpha-methyl styrene, chlorostyrene, vinyl toluene, divinyl benzene, dially phthalate, alkyl methacrylates and alkyl acrylates. In one embodiment, the co-monomers include thermoplastic and elastomeric monomers.

The main polymerization of an olefin is typically carried out in the gaseous or liquid phase. In one embodiment, the main polymerization employs a catalyst system containing the solid catalyst component in an amount from about 0.001 to about 0.75 millimoles calculated as Ti atom per liter of the volume of the polymerization zone, the organoaluminum compound in an amount from about 1 to about 2,000 moles per mole of titanium atoms in the solid catalyst component, and the organosilicon compound in an amount from about 0.001 to about 10 moles calculated as Si atoms in the organosilicon compound per mole of the metal atoms in the organoaluminum compound.

In another embodiment, the main polymerization employs a catalyst system containing the solid catalyst component in an amount of from about 0.005 to about 0.5 millimoles calculated as Ti atom per liter of the volume of the polymerization zone, the organoaluminum compound in an amount from about 5 to about 500 moles per mole of titanium atoms in the solid catalyst component, and the organosilicon compound in an amount from about 0.01 to about 2 moles calculated as Si atoms in the organosilicon compound per mole of the metal atoms in the organoaluminum compound. In yet another embodiment, the main polymerization employs a catalyst system containing the alkyl benzoate derivative in an amount from about 0.005 to about 1 mole calculated as Si atoms in the organosilicon compound per mole of the metal atoms in the organoaluminum compound.

When the organoaluminum compound and the organosilicon compound are used partially in the preliminary polymerization, the catalyst system subjected to the preliminary polymerization is used together with the remainder of the catalyst system components. The catalyst system subjected to the preliminary polymerization may contain the product of the preliminary polymerization.

The use of hydrogen at the time of polymerization promotes and contributes to control of the molecular weight of the resulting polymer, and the polymer obtained may have a desirable melt flow rate. The stereoregularity index of the resulting polymer and the activity of the catalyst system are thereby increased when the methods and systems of embodiments of the presently disclosed and claimed inventive concept(s) are utilized.

In one embodiment, the polymerization temperature in the main polymerization is from about 20 degrees Celsius to about 200 degrees Celsius. In another embodiment, the polymerization temperature in the main polymerization is from about 50 degrees Celsius to about 180 degrees Celsius. In one embodiment, the polymerization pressure in the main polymerization is typically from atmospheric pressure to about 100 kg/cm². In another embodiment, the polymerization pressure in the main polymerization is typically from about 2 kg/cm² to about 50 kg/cm². The main polymerization may be carried out batchwise, semi-continuously or continuously. The main polymerization may also be carried out in two or more stages under different reaction conditions.

The olefin polymer so obtained may be a homopolymer, a random copolymer, a block copolymer or an impact copolymer. The impact copolymer contains an intimate mixture of a polyolefin homopolymer and a polyolefin rubber. Examples of polyolefin rubbers include ethylene propylene rubber (EPR) such as ethylene propylene methylene copolymer rubber (EPM) and ethylene propylene diene methylene terpolymer rubber (EPDM).

The olefin polymer obtained by using the catalyst system has a very small amount of an amorphous polymer component and therefore a small amount of a hydrocarbon-soluble component. Accordingly, a film molded from the resultant polymer has low surface tackiness.

The polyolefin obtained by the polymerization process is excellent in particle size distribution, particle diameter and bulk density, and the copolyolefin obtained has a narrow composition distribution. In an impact copolymer, excellent fluidity, low temperature resistance, and a desired balance between stiffness and elasticity can be obtained.

In one embodiment, propylene and an alpha-olefin having 2 or from about 4 to about 20 carbon atoms are copolymerized in the presence of the catalyst system described above. The catalyst system may be one subjected to the preliminary polymerization described above. In another embodiment, propylene and an ethylene rubber are formed in two reactors coupled in series to form an impact polymer.

The alpha-olefin having 2 carbon atoms is ethylene, and examples of the alpha-olefin having about 4 to about 20 carbon atoms are 1-butene, 1-pentene, 4-methyl-1-pentene, 1-octene, 1-hexene, 1-methyl-1-pentene, 3-methyl-1-pentene, 3-methyl-1-butene, 1-decene, vinylcyclohexane, 1-tetradecene, and the like.

In the main polymerization, propylene may be copolymerized with two or more such alpha-olefins. For example, it is possible to copolymerize propylene with ethylene and 1-butene. In one embodiment, propylene is copolymerized with ethylene, 1-butene or ethylene and 1-butene.

Block copolymerization of propylene and another alpha-olefin may be carried out in two stages. The polymerization in a first stage may be the homopolymerization of propylene or the copolymerization of propylene with the other alpha-olefin. In one embodiment, the amount of the monomers polymerized in the first stage is from about 50 to about 95% by weight. In another embodiment, the amount of the monomers polymerized in the first stage is from about 60 to about 90% by weight. This first stage polymerization may, as required, be carried out in two or more stages under the same or different polymerization conditions.

In one embodiment, the polymerization in a second stage is desirably carried out such that the mole ratio of propylene to the other alpha-olefin(s) is from about 10/90 to about 90/10. In another embodiment, the polymerization in a second stage is desirably carried out such that the mole ratio of propylene to the other alpha-olefin(s) is from about 20/80 to about 80/20. In yet another embodiment, the polymerization in a second stage is desirably carried out such that the mole ratio of propylene to the other alpha-olefin(s) is from about 30/70 to about 70/30. Producing a crystalline polymer or copolymer of another alpha-olefin may be provided in the second polymerization stage.

The propylene copolymer so obtained may be a random copolymer or the above-described block copolymer. This propylene copolymer typically contains from about 7 to about 50 mole % of units derived from the alpha-olefin having 2 or from about 4 to about 20 carbon atoms. In one embodiment, a propylene random copolymer contains from about 7 to about 20 mole % of units derived from the alpha-olefin having 2 or from about 4 to about 20 carbon atoms. In another embodiment, the propylene block copolymer contains from about 10 to about 50 mole % of units derived from the alpha-olefin having 2 or 4-20 carbon atoms.

In another embodiment, copolymers made with the catalyst system contain from about 50% to about 99% by weight poly-alpha-olefins and from about 1% to about 50% by weight co-monomers (such as thermoplastic or elastomeric monomers). In another embodiment, copolymers made with the catalyst system contain from about 75% to about 98% by weight poly-alpha-olefins and from about 2% to about 25% by weight co-monomers.

It should be understood that where there is no reference to a particular polyunsaturated compound, the method of polymerization, the amount of the catalyst system and the polymerization conditions, the same description as any of the above embodiments are applicable and would be apparent to one of ordinary skill in the art.

The catalysts/methods can, in some embodiments, produce poly-alpha-olefins having xylene soluble (XS) from about 0.5% to about 10%. In another embodiment, poly-alpha-olefins having xylene soluble (XS) from about 1.5% to about 8% are produced. XS refers to the percent of solid polymer that dissolves into xylene. A low XS % value generally corresponds to a highly isotactic polymer (i.e. higher crystallinity), whereas a high XS % value generally corresponds to a low isotactic polymer.

In one embodiment, the catalyst efficiency (measured as kilogram of polymer produced per gram of catalyst) of the catalyst system is at least about 20. In another embodiment, the catalyst efficiency of the catalyst system is at least about 40.

The catalysts/methods can in some instances lead to the production of poly-alpha-olefins having melt flow indexes (MFI) from about 0.1 to about 100. The MFI is measured according to ASTM standard D1238. In another embodiment, poly-alpha-olefins having an MFI from about 5 to about 30 are produced. In one embodiment, an impact polypropylene-ethylenepropylene rubber product has an MFI from about 4 to about 10. In another embodiment, an impact polypropylene-ethylenepropylene rubber product has an MFI from about 5 to about 9. In some instances a relatively high MFI indicates relatively high catalyst efficiency is obtainable.

The catalysts/methods can in some instances lead to the production of poly-alpha-olefins have bulk densities (BD) of at least about 0.3 cc/g. In another embodiment, poly-alpha-olefins having a BD of at least about 0.4 cc/g.

In one embodiment, an impact polypropylene-ethylenepropylene rubber product having a BD of at least about 0.3 cc/g is produced. In another embodiment, an impact polypropylene-ethylenepropylene rubber product having a BD of at least about 0.4 cc/g is produced.

The catalysts/methods of the presently disclosed and claimed inventive concept(s) lead to the production of poly-alpha-olefins having from a relatively narrow to a broad molecular weight distribution depending on the catalyst composition. Polydispersive Index (PI) is strictly connected with the molecular weight distribution of the polymer. PI is calculated as the weight average molecular weight divided by the number average molecular weight, PI=M_(w)/M_(n). In one embodiment, the PI of a polypropylene polymer made with the catalyst system is from about 2 to about 8. In another embodiment, the PI of a polypropylene polymer made with the catalyst system is from about 4 to about 7.

The disclosed methods can lead to the production of a propylene block copolymer and impact copolymers including polypropylene based impact copolymer having one or more excellent melt-flowability, moldability desirable balance between rigidity and elasticity, good stereospecific control, good control over polymer particle size, shape, size distribution, and molecular weight distribution, and impact strength with a high catalytic efficiency and/or good operability. Employing the catalyst systems containing the solid catalyst component yields catalysts simultaneously having high catalytic efficiency, and one or more of excellent melt-flowability, extrudability, moldability, rigidity-elasticity and impact strength.

Examples of systems for polymerizing olefins are now described. Referring to FIG. 1, a high level schematic diagram of a system 10 for polymerizing olefins is shown. Inlet 12 is used to introduce into a reactor 14 catalyst system components, olefins, optional co-monomers, hydrogen gas, fluid media, pH adjusters, surfactants, and any other additives. Although only one inlet is shown, many often are employed. Reactor 14 is any suitable vehicle that can polymerize olefins. Examples of reactor 14 include a single reactor, a series of two or more reactors, slurry reactors, fixed bed reactors, gas phase reactors, fluidized gas reactors, loop reactors, multizone circulating reactors, and the like. Once polymerization is complete, or as polyolefins are produced, the polymer product is removed from the reactor 14 via outlet 16 which leads to a collector 18. Collector 18 may include downstream processing, such as heating, extrusion, molding, and the like.

Referring to FIG. 2, a schematic diagram of a multizone circulating reactor 20 that can be employed as the reactor 14 in FIG. 1 or the reactor 44 in FIG. 3 for making polyolefins is shown. The multizone circulating reactor 20 substitutes a series of separate reactors with a single reactor loop that permits different gas phase polymerization conditions in two sides due to use of a liquid barrier. In the multizone circulating reactor 20, a first zone starts out rich in olefin monomers, and optionally one or more co-monomers. A second zone is rich in hydrogen gas, and a high velocity gas flow divides the growing resin particles out loosely. The two zones produce resins of different molecular weights and/or monomer compositions. Polymer granules grow as they circulate around the loop, building up alternating layers of each polymer fraction in an onion like fashion. Each polymer particle constitutes an intimate combination of both polymer fractions.

In operation, the polymer particles pass up through the fluidizing gas in an ascending side 24 of the loop and come down through the liquid monomer on a descending side 26. The same or different monomers (and again optionally one or more co-monomers) can be added in the two reactor legs. The reactor uses the catalyst system described above.

In the liquid/gas separation zone 30, hydrogen gas is removed to cool and recirculate. Polymer granules are then packed into the top of the descending side 26, where they then descend. Monomers are introduced as liquids in this section. Conditions in the top of the descending side 26 can be varied with different combinations and/or proportions of monomers in successive passes.

Referring to FIG. 3, a high level schematic diagram of another system 40 for polymerizing olefins is shown. This system is ideally suited to make impact polymers. A reactor 44, such as a single reactor, a series of reactors, or a multizone circulating reactor is paired with a second reactor 48, such as a gas phase or a fluidized bed reactor, downstream containing the catalyst systems described above to make impact copolymers with desirable impact to stiffness balance or greater softness than made with conventional catalyst systems. Inlet 42 is used to introduce into the reactor 44 catalyst system components, olefins, optional co-monomers, hydrogen gas, fluid media, pH adjusters, surfactants, and any other additives. Although only one inlet is shown, many often are employed. Through transfer means 46 the polyolefin made in the first reactor 44 is sent to a second reactor 48. Feed 50 is used to introduce catalyst system components, olefins, optional co-monomers, fluid media, and any other additives. The second reactor 48 may or may not contain catalyst system components. Again, although only one inlet is shown, many often are employed. Once the second polymerization is complete, or as impact copolymers are produced, the polymer product is removed from the second reactor 48 via outlet 52 which leads to a collector 54. Collector 54 may include downstream processing, such as heating, extrusion, molding, and the like. At least one of the first reactor 44 and the second reactor 48 contains catalyst systems in accordance with an embodiment of the invention.

When making an impact copolymer, polypropylene can be formed in the first reactor while an ethylene propylene rubber can be formed in the second reactor. In this polymerization, the ethylene propylene rubber in the second reactor is formed with the matrix (and particularly within the pores) of the polypropylene formed in the first reactor. Consequently, an intimate mixture of an impact copolymer is formed, wherein the polymer product appears as a single polymer product. Such an intimate mixture cannot be made by simply mixing a polypropylene product with an ethylene propylene rubber product.

Although not shown in any of the figures, the systems and reactors can be controlled, optionally with feedback based on continuous or intermittent testing, using a processor equipped with an optional memory and controllers. For example, a processor may be connected to one or more of the reactors, inlets, outlets, testing/measuring systems coupled with the reactors, and the like to monitor and/or control the polymerization process, based on preset data concerning the reactions, and/or based on testing/measuring data generated during a reaction. The controller may control valves, flow rates, the amounts of materials entering the systems, the conditions (temperature, reaction time, pH, etc.) of the reactions, and the like, as instructed by the processor. The processor may contain or be coupled to a memory that contains data concerning various aspects of the polymerization process.

With respect to any figure or numerical range for a given characteristic, a figure or a parameter from one range may be combined with another figure or a parameter from a different range for the same characteristic to generate a numerical range.

Other than in the operating examples, or where otherwise indicated, all numbers, values and/or expressions referring to quantities of ingredients, reaction conditions, etc., used in the specification and claims are to be understood as modified in all instances by the term “about.”

EXAMPLES

The following examples illustrate embodiments of the presently disclosed and claimed inventive concept(s). Unless otherwise indicated in the following examples and elsewhere in the specification and claims, all parts and percentages are by weight, all temperatures are in degrees Celsius, and pressure is at or near atmospheric pressure.

Bulk Propylene Polymerization

Triethyl aluminum (1.5 cc at 25 wt %), cyclohexylmethyldimethoxysilane (76.8 mmol) and 10 mg of the solid catalyst component dispersed into 1 ml of mineral oil was introduced into a 3.4-liter stainless steel autoclave, which was thoroughly purged with nitrogen. The autoclave was pressurized to 10 psi with nitrogen and 32 mmol of hydrogen. The autoclave was then filled with 1500 ml of liquid propylene and the temperature was raised to 70° C. The temperature was maintained at 70 degrees. Propylene was polymerized for 1 hour. At the end of polymerization, the reactor was cooled down to 35° C. and the polymer was removed. CE refers to catalytic efficiency to produce polypropylene (PP), XS refers to xylene solubles, and MFI refers to melt flow index.

Example 1

The catalyst synthesis was conducted in a 1 L Buchi reactor. The reactor was charged with 13.2 g of MgCl₂, 204 g of toluene, 25.6 g of Epichlorohydrin (ECH), and 26.8 g of tributyl phosphate (TBP). The contents of the reactor were heated and agitated at 60° C. for 5 h. 3.2 g of phthalic anhydride (PA) was added. The reactor was cooled down to −25° C. and TiCl₄ (261 g) was added. The reactor was heated up to 85° C. and 2.6 g of diisooctyl phthalate (DIOP) was added (Step 1). The mixture was heated for 1 h and liquid was filtered off. 130 ml of toluene was added with 2.0 g of naphthalene-1,8-diyl dibenzoate (“THANE”) (Step 2). The mixture was heated at 80° C. for 1 h. After filtering off the liquid, the solid was washed with toluene and activated with 10% vol TiCl₄/toluene at 95° C. for 1 h in presence of 3.6 g of DIOP (Step 3). Three additional activations were conducted at 110° C. for 30 min. The catalyst was washed with hexane and dried under vacuum. Tested activity: 72.1 kg/g, XS %: 1.91%, MFI: 0.7 g/10 min.

Melt flow index or MFI is a measure of the ease of flow of the melt of a thermoplastic polymer. It is defined as the mass of polymer, in grams, flowing in ten minutes through a capillary of a specific diameter and length by a pressure applied via prescribed alternative gravimetric weights for alternative prescribed temperatures. Melt flow rate is an indirect measure of molecular weight, with high melt flow rate corresponding to low molecular weight. At the same time, melt flow rate is a measure of the ability of the material's melt to flow under pressure.

Example 2 (Comparative)

The experiment was conducted as described in Example 1, except for Steps 1-3. In Step 1 of Example 2, the reactor was heated up to 85° C. and 2.4 g of THANE was added. In Step 2 of Example 2, 130 ml of toluene was added with 1.0 g of THANE. In Step 3 of Example 2, after filtering off the liquid, the solid was washed with toluene and activated with 10% vol TiCl₄/toluene at 105° C. for 1 h in presence of 3.6 g of THANE. Tested activity: 62.7 kg/g, XS: 2.44%, MFI: 0.2 g/10 min.

Example 3 (Comparative)

The experiment was conducted as described in Example 1, except for Steps 1-3. In Step 1 of Example 3, the reactor was heated up to 85° C. and 2.6 g of DIOP was added. In Step 2 of Example 3, 130 ml of toluene was added with 6.5 g of DIOP. In Step 3 of Example 3, after filtering off the liquid, the solid was washed with toluene and activated with 10% vol TiCl₄/toluene at 95° C. for 1 h in presence of 3.2 g of DIOP. Tested activity: 46.6 kg/g, XS: 2.55%, MFI: 2.9 g/10 min.

Examples 4-8

Examples 4-8 and Table 1 were prepared according to Example 1, unless otherwise noted. The internal electron donors were added separately in three different places: Step 1, Step 2, and Step 3.

TABLE 1 Hybrid Catalyst with DIOP and THANE MFI D (Step 1) D (Step 2) D (Step 3) CE XS g/10 Ex g g g Ti % DIOP % THANE % kg/g % min 4 1.0 8.0 7.0 1.43 12.04 7.17 61.9 1.54 1.1 (THANE) (DIOP) (DIOP) 5 2.6 6.5 0.6 2.28 12.53 2.68 57.9 2.55 3.2 (DIOP) (DIOP) (THANE) 6 2.0 0.6 7.0 1.80 8.41 11.74 67.6 1.63 1.0 (THANE) (THANE) (DIOP) 7 2.6 0.6 3.6 1.89 11.74 2.84 56.3 2.28 2.5 (DIOP) (THANE) (DIOP) 8 0.6 6.5 3.6 1.82 13.03 2.71 58.0 2.29 4.2 (THANE) (DIOP) (DIOP)

Examples 9-15

Examples 9-15 and Table 2 were prepared the same way as those for Examples 4-8, except diisononyl phthalate (DINP) was used instead of diisooctyl phthalate (DIOP).

TABLE 2 Hybrid Catalyst with DINP and THANE MFI D (Step 1) D (Step 2) D (Step 3) CE XS g/10 Ex g g g Ti % DINP % THANE % kg/g % min 9 0.7 6.5 3.6 1.69 15.14 3.20 61.6 2.31 1.6 (THANE) (DINP) (DINP) 10 2.7 6.5 3.2 1.72 14.42 3.20 55.9 2.31 1.8 (DINP) (DINP) (DINP), + 0.6 (THANE) 11 2.7 6.5 0.8 1.93 12.44 4.00 56.9 2.72 2.9 (DINP) (DINP) (THANE) 12 2.7 6.5 0.8 1.90 11.13 5.68 58.8 2.53 1.3 (DINP) (DINP) (THANE) 13 2.7 0.8 6.0 1.47 14.15 3.53 53.4 2.52 3.0 (DINP) (THANE) (DINP) 14 0.6 6.0 4.0 1.69 14.80 3.29 56.7 2.18 1.9 (THANE) (DINP) (DINP) 15 2.7 6.0 0.6 2.06 13.21 3.05 59.8 2.68 2.5 (DINP) (DINP) (THANE)

Example 16 (Comparative)

The experiment was conducted as described in Example 1, except for Steps 1-3. In Step 1 of Example 16, the reactor was heated up to 85° C. and 2.7 g of DINP was added. In Step 2 of Example 16, 130 ml of toluene was added with 5.0 g of DINP. In Step 3 of Example 16, after filtering off the liquid, the solid was washed with toluene and activated with 10% vol TiCl₄/toluene at 95° C. for 1 h in presence of 3.2 g of DINP. Tested activity: 47.0 kg/g, XS: 3.01%, MFI: 2.6 g/10 min.

Examples 17-18

Examples 17-18 and Table 3 were prepared the same way as Examples 4-8, except dioctyl phthalate (DOP) was used instead of diisooctyl phthalate (DIOP).

TABLE 3 Hybrid Catalyst with DOP and THANE MFI D (Step 1) D (Step 2) D (Step 3) CE XS g/10 Ex g g g Ti % DOP % THANE % kg/g % min 17 2.7 6.5 0.7 2.09 11.93 4.2 55.9 2.85 2.9 (DOP) (DOP) (THANE) 18 2.7 0.8 3.6 1.87 11.10 4.1 57.3 3.37 5.8 (DOP) (THANE) (DOP)

Example 19 (Comparative)

The experiment was conducted as described in Example 1, except for Steps 1-3. In Step 1 of Example 19, the reactor was heated up to 85° C. and 2.5 g of DOP was added. In Step 2 of Example 19, 130 ml of toluene was added with 5.5 g of DOP. In Step 3 of Example 19, after filtering off the liquid, the solid was washed with toluene and activated with 10% vol TiCl₄/toluene at 95° C. for 1 h in presence of 3.2 g of DOP. Tested activity: 44.8 kg/g, XS: 2.86%, MFI: 9.3 g/10 min.

Examples 20-21

Examples 20-21 and Table 4 were prepared in the same manner as Examples 4-8, except bis(2-propylheptyl) phthalate (DPHP) was used instead of diisooctyl phthalate (DIOP).

TABLE 4 Hybrid Catalyst with DPHP and THANE MFI D (Step 1) D (Step 2) D (Step 3) CE XS g/10 Ex g g g Ti % DPHP % THANE % kg/g % min 20 2.7 6.5 0.7 2.15 n/a 3.72 57.9 3.21 2.4 (DPHP) (DPHP) (THANE) 21 0.7 6.5 4.0 1.80 n/a 3.52 57.0 2.78 3.5 (THANE) (DPHP) (DPHP)

Example 22 (Comparative)

The experiment was conducted as described in Example 1, except for Steps 1-3. In Step 1 of Example 22, the reactor was heated up to 85° C. and 2.8 g of DPHP was added. In Step 2 of Example 22, 130 ml of toluene was added with 5.8 g of DPHP. In Step 3 of Example 22, after filtering off the liquid, the solid was washed with toluene and activated with 10% vol TiCl₄/toluene at 95° C. for 1 h in presence of 4.0 g of DPHP. Tested activity: 43.1 kg/g, XS: 3.47%, MFI: 8.2 g/10 min.

Example 23

Example 23 and Table 5 were prepared in the same manner as Examples 4-8, except dibutyl phthalate (DNBP) was used instead of diisooctyl phthalate (DIOP).

TABLE 5 Hybrid Donor Catalyst with DNBP and THANE MFI D (Step 1) D (Step 2) D (Step 3) CE XS g/10 Ex g g g Ti % DNBP % THANE % kg/g % min 23 5.0 3.0 0.8 1.64 11.92 3.84 49.0 2.21 3.9

Examples 24-31

Examples 24-31 and Table 6 were prepared according to Example 1, unless otherwise noted. The internal electron donors were added separately in three different places: step 1, step 2 and step 3. The examples demonstrate that the combination of two internal donors: DINCH and THANE results in variable catalyst properties and has a synergistic affect. It is interesting to note that variations in the donor placements affect the isotacticity and molecular weight (MFI) of polymer produced.

TABLE 6 Catalysts with DINCH and THANE MFI D (Step 1) D (Step 2) D (Step 3) CE XS g/10 Ex g g g Ti % DINCH % THANE % kg/g % min 24 0.8 10.0  0.4 2.00 n/a 6.26 56.4 2.82 1.6 (THANE) (DINCH) (THANE) 25 0.7 6.0  6.0 2.09 n/a 3.70 56.9 2.30 2.2 (THANE) (DINCH) (DINCH) 26 0.7 12.0 1.75 4.76 3.88 47.4 3.00 4.0 (THANE) (DINCH) 27 0.8 12.0 1.73 3.60 4.30 49.3 3.13 2.7 (THANE) (DINCH 28 0.4 0.4 10.0 2.01 4.20 3.80 46.3 3.54 3.6 (THANE) (THANE) (DINCH 29 0.6 12.0 1.78 4.86 3.42 39.1 3.05 4.1 (THANE) (DINCH) 30 8.9 2.22 3.74 no 19.1 7.57 7.7 (DINCH) 31 12.6 1.95 4.77 no 13.7 6.92 4.1 (DINCH) Note that Examples 30 and 31 are comparative examples.

Example 32

The experiment was conducted as described in Example 1, except for Steps 1-3. In Step 1 of Example 32, the reactor was heated up to 85° C. and 0.7 g of THANE was added. In Step 2 of Example 32, 130 ml of toluene was added with 7.0 g of ethyl benzoate. In Step 3 of Example 32, after filtering off the liquid, the solid was washed with toluene and activated with 10% vol TiCl₄/toluene at 95° C. for 1 h in presence of 6.0 g of ethyl benzoate. Tested activity: 31.9 kg/g, XS: 6.02%, MFI: 6.0 g/10 min.

Example 33-35

Examples 33-35 and Table 7 were prepared in the same manner as Examples 4-8, except tridecyl methacrylate (TDMA) was used instead of diisooctyl phthalate (DIOP).

TABLE 7 Catalysts with TDMA and THANE MFI D (Step 2) D (Step 3) CE XS g/10 Ex g g Ti % TDMA % THANE % kg/g % min 33 2.0 2.0 3.16 11.8 11.8 51.3 2.08 1.9 (TDMA) (THANE) 34 6.0 no 2.65 11.2 11.2 51.9 1.8 1.5 (TDMA), + 2.0 (THANE) 35 2.0 no 3.37 no 8.9 53.1 2.67 1.1 (THANE)

Note that Example 35 is a comparative example. The catalysts of Examples 33 and 34 demonstrate higher isotacticity and higher MFI in comparison with Example 35, which used only a single donor.

Examples 36-48 General Reaction 1

3.3 g of MgCl, 0.8 g of phthalic anhydride, 6.41 g of epichlorohydrin, 6.70 g of tributylphosphate, and 40.92 g of toluene were added to a 250 ml reactor under nitrogen. The mixture was heated to 60° C. and agitated at 400 rpm for 2 hours. The mixture was cooled to −30° C., then 65 g of TiCl₄ was added, and the reactor was maintained at −25° C. during the addition. The agitation was reduced to 200 rpm and the reactor was heated to 85° C. for two hours. After that, the agitation was increased to 400 rpm for 30 minutes. Next, 1.5 mmol of a 1,8-naphthyl diester compound was added, stirred for one hour, and then filtered. Next, 38 ml of toluene and 4.48 mmol of a secondary internal donor compound were added into the reactor and the mixture was heated to 85° C. at 400 rpm, stirred for one hour, and then filtered. The heat was turned off, and the mixture was washed with 65 ml of toluene and filtered. Another 65 ml of toluene was added and the mixture was hold under nitrogen overnight without stirring. The toluene was removed by filtering, and 66.25 ml of 10% wt TiCl₄-toluene were added and the mixture was heated to 95° C. at 400 rpm for one hour and filtered. The previous step was repeated 3 times at 110° C., 400 rpm, and 30 minute each. The final catalyst was washed 4 times with 65 ml of hexane and collected as a hexane slurry.

Example 36

The reaction procedure for General Reaction 1 was followed, except naphthalene-1,8-diyl dibenzoate (hereafter “THANE”) was used as the 1,8-naphthyl diester compound and no secondary internal donor compound was added.

Example 37

The reaction procedure for General Reaction 1 was followed, except no 1,8-naphthyl diester compound was used and butyl 2-methoxy-1-naphthoate was added as the secondary internal donor compound, which is a compound of general formula (II).

Example 38

The reaction procedure for General Reaction 1 was followed, except naphthalene-1,8-diyl dibenzoate was used as the 1,8-naphthyl diester compound (see Example 36) and butyl 2-methoxy-1-naphthoate (see Example 37) was added as the secondary internal donor compound, which is a compound of general formula (II).

Example 39

The reaction procedure for General Reaction 1 was followed, except no 1,8-naphthyl diester compound was used and 7-methyloctyl 2-methoxy-1-naphthoate was added as the secondary internal donor compound, which is a compound of general formula (II).

Example 40

The reaction procedure for General Reaction 1 was followed, except naphthalene-1,8-diyl dibenzoate was used as the 1,8-naphthyl diester compound (see Example 36) and 7-methyloctyl 2-methoxy-1-naphthoate (see Example 39) was added as the secondary internal donor compound, which is a compound of general formula (II).

Example 41

The reaction procedure for General Reaction 1 was followed, except no 1,8-naphthyl diester compound was used and butyl 2-methoxybenzoate was added as the secondary internal donor compound, which is a compound of general formula (III).

Example 42

The reaction procedure for General Reaction 1 was followed, except naphthalene-1,8-diyl dibenzoate was used as the 1,8-naphthyl diester compound (see Example 36) and butyl 2-methoxybenzoate (see Example 41) was added as the secondary internal donor compound, which is a compound of general formula (III).

Example 43

The reaction procedure for General Reaction 1 was followed, except no 1,8-naphthyl diester compound was used and butyl 2,6-dimethoxybenzoate was added as the secondary internal donor compound, which is a compound of general formula (IV).

Example 44

The reaction procedure for General Reaction 1 was followed, except naphthalene-1,8-diyl dibenzoate was used as the 1,8-naphthyl diester compound (see, Example 36) and butyl 2,6-dimethoxybenzoate (see, Example 43) was added as the secondary internal donor compound, which is a compound of general formula (IV).

Example 45

The reaction procedure for General Reaction 1 was followed, except no 1,8-naphthyl diester compound was used and 7-methyloctyl 2,6-dimethoxybenzoate was added as the secondary internal donor compound, which is a compound of general formula (IV).

Example 46

The reaction procedure for General Reaction 1 was followed, except naphthalene-1,8-diyl dibenzoate was used as the 1,8-naphthyl diester compound (see Example 36) and 7-methyloctyl 2,6-dimethoxybenzoate (see Example 45) was added as the secondary internal donor compound, which is a compound of general formula (IV).

Example 47

The reaction procedure for General Reaction 1 was followed, except no 1,8-naphthyl diester compound was used and (2-methoxyphenyl)(pyrrolidin-1-yl)methanone was added as the secondary internal donor compound, which is a compound of general formula (V).

Example 48

The reaction procedure for General Reaction 1 was followed, except naphthalene-1,8-diyl dibenzoate was used as the 1,8-naphthyl diester compound (see Example 36) and (2-methoxyphenyl)(pyrrolidin-1-yl)methanone (see Example 47) was added as the secondary internal donor compound, which is a compound of general formula (V).

The results of Examples 36-48 are provided in Table 8, which compares a combination of the internal electron donors to control examples of internal electron donors used individually. Examples 36-48 demonstrate that a catalyst prepared with two different internal donors are different in comparison with the catalyst when the internal donors are used individually. The activities of catalysts with the two internal donors are higher in comparison with the catalyst having a single internal donor. The catalyst composition using at least two different donors provide a synergistic affect resulting in variable catalyst and polymer properties.

TABLE 8 Combination of Internal Electron Donor vs. Individual Electron Donors Xylene naphthalene-1,8-diyl Secondary Internal Activity soluble PP MFI Ex dibenzoate Electron Donor(s) (Kg/g · h) (% XS) (g/10 min) 36 naphthalene-1,8-diyl none 48.9 2.64 0.3 dibenzoate (P-1) 37 none butyl 2-methoxy-1- 33.6 6.56 14.7 naphthoate (S-IIa) 38 naphthalene-1,8-diyl butyl 2-methoxy-1- 61.3 3.45 0.4 dibenzoate (P-1) naphthoate (S-IIa) 39 none 7-methyloctyl 2-methoxy- 36.9 7.4 9 1-naphthoate (S-IIb) 40 naphthalene-1,8-diyl 7-methyloctyl 2-methoxy- 65.6 2.81 0.4 dibenzoate (P-1) 1-naphthoate (S-IIb) 41 none butyl 2-methoxybenzoate 30.5 high high (S-III) 42 naphthalene-1,8-diyl butyl 2-methoxybenzoate 55.4 2.95 0.3 dibenzoate (P-1) (S-III) 43 none butyl 2,6-dimethoxy 28.9 7.4 8.3 benzoate (S-IVa) 44 naphthalene-1,8-diyl butyl 2,6-dimethoxy 55.4 2.95 0.3 dibenzoate (P-1) benzoate (S-IVa) 45 none 7-methyloctyl 2,6-dimethoxy 27.5 high high benzoate (S-IVb) 46 naphthalene-1,8-diyl 7-methyloctyl 2,6-dimethoxy 53.8 2.51 0.2 dibenzoate (P-1) benzoate (S-IVb) 47 none (2-methoxyphenyl) 25.1 6.21 high (pyrrolidin-1- yl)methanone (S-V) 48 naphthalene-1,8-diyl (2-methoxyphenyl) 58.9 2.12 0.4 dibenzoate (P-1) (pyrrolidin-1- yl)methanone (S-V)

Example 49-58

The dispersity index (PI) measurement.

The stabilized polymer sample is pressed on a hot press to make a plate. The polymer plate is then analyzed on a Rheometer at certain temperatures. From the data plot, P I is calculated using built in molecular weight distribution (MWD) software. PI is obtained from the rheological curve and is proportional to the polydispersity of the polymer MWD.

Examples 49-58 demonstrate that polydispersity of polymers produced with the hybride catalysts is variable based on the internal donors used and the catalyst composition. The combination of THANE with DINCH or EB on the catalyst allows production of polypylene with high polydispersity index.

TABLE 9 Examples of Rheological properties of homo polypropylene Polypropylene Example from example Donors in catalyst PI, 49 (comparison) 2 THANE 4.410 50 20 DPHP/THANE 4.6998 51 4 DIOP/THANE 4.5942 52 25 DINCH/THANE 4.6053 53 24 DINCH/THANE 4.9194 54 28 DINCH/THANE 5.0620 55 27 DINCH/THANE 5.1012 56 29 DINCH/THANE 5.2285 57 32 EB/THANE 5.5720 58 33 TDMA/THANE 5.0742

It is, of course, not possible to describe every conceivable combination of the components or methodologies for purposes of describing the disclosed information, but one of ordinary skill in the art can recognize that many further combinations and permutations of the disclosed information are possible. Accordingly, the disclosed information is intended to embrace all such alternations, modifications and variations that fall within the spirit and scope of the appended claims. Furthermore, to the extent that the term “includes,” “has,” “involve,” or variants thereof is used in either the detailed description or the claims, such term is intended to be inclusive in a manner similar to the term “comprising” as “comprising” is interpreted when employed as a transitional word in a claim. 

1. A solid catalyst component for use in olefinic polymerization, comprising: titanium compound, magnesium compound, halogen, and a combination of internal electron donor compounds, wherein said combination of internal electron donor compounds comprises at least one 1,8-naphthyl diester compound represented by general formula (I):

wherein R₁ and R₂ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens, and wherein R₃, R₄, R₅, R₆, R₇, and R₈ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; and at least one secondary internal donor compound selected from the group consisting of mono- or poly-carboxylic esters, ethers, ketones, organic compounds containing carboxylic and ether groups, organic compounds containing carboxylic groups and carbonyl groups, and organic compounds containing carboxylic groups, ether groups, and carbonyl groups.
 2. The solid catalyst component according to claim 1, wherein the secondary internal donor compound is selected from the group consisting of: a compound represented by general formula (II):

a compound represented by general formula (III):

a compound represented by general formula (IV):

a compound represented by general formula (V):

a compound represented by general formula (VI):

a compound represented by general formula (VII):

a compound represented by general formula (VIII):

combinations thereof, wherein R₉ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₀ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₁, R₁₂, R₁₃, R₁₄, R₁₅, and R₁₆ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₇ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₈ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₁₉, R₂₀, R₂₁, and R₂₂ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₂₃, R₂₄, and R₂₅ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₂₆ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₂₇, R₂₈, R₂₉, and R₃₀ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₃₁, R₃₂, R₃₃, R₃₄, R₃₅, R₃₆, R₃₇, and R₃₈ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₃₉ and R₄₀ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH—₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₄₁, R₄₂, R₄₃, and R₄₄ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₄₅ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₄₆ is selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; R₄₇ and R₄₈ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens; and R₄₉, R₅₀, R₅₁, and R₅₂ are each independently selected from the group consisting of a hydrogen; a halogen; and a linear or branched, cyclic or acyclic, saturated or non-saturated C₁ to C₂₂ hydrocarbyl group, wherein the hydrocarbyl group optionally contains a —O—, —NH—, or —S— group in place of a —CH₂— group or a —N═ group in place of a —C═ group, and wherein the hydrocarbyl group is optionally substituted by one or more halogens.
 3. The solid catalyst component according to claim 2, wherein said 1,8-naphthyl diester compound of the general formula (I) is selected from the group consisting of naphthalene-1,8-diyl dibenzoate, 8-(benzoyloxy)naphthalen-1-yl 2-methylbenzoate, 8-(benzoyloxy)naphthalen-1-yl 3-methylbenzoate, 8-(benzoyloxy)naphthalen-1-yl 4-methylbenzoate, 8-(benzoyloxy)naphthalen-1-yl 2,4,6-trimethylbenzoate, 8-(benzoyloxy)naphthalen-1-yl isonicotinate, 8-(benzoyloxy)naphthalen-1-yl nicotinate, 8-(benzoyloxy)naphthalen-1-yl picolinate, 8-((cyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-((cyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-((2-methylcyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-((3-methylcyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-((4-methylcyclohexanecarbonyl)oxy)naphthalen-1-yl benzoate, 8-(propionyloxy)naphthalen-1-yl benzoate, 8-(butyryloxy)naphthalen-1-yl benzoate, 8-(pentanoyloxy)naphthalen-1-yl benzoate, 8-(benzoyloxy)naphthalen-1-yl tetrahydro-2H-pyran-4-carboxylate, 8-(benzoyloxy)naphthalen-1-yl piperidine-4-carboxylate, and 8-(benzoyloxy)naphthalen-1-yl tetrahydro-2H-thiopyran-4-carboxylate.
 4. The solid catalyst component according to claim 2, wherein the secondary internal donor compound includes a compound represented by general formula (II) as selected from the group consisting of 2-methoxy-1-naphthoic acid, methyl 2-methoxy-1-naphthoate, ethyl 2-methoxy-1-naphthoate, propyl 2-methoxy-1-naphthoate, butyl 2-methoxy-1-naphthoate, pentyl 2-methoxy-1-naphthoate, hexyl 2-methoxy-1-naphthoate, heptyl 2-methoxy-1-naphthoate, octyl 2-methoxy-1-naphthoate, nonyl 2-methoxy-1-naphthoate, undecyl 2-methoxy-1-naphthoate, dodecyl 2-methoxy-1-naphthoate, tridecyl 2-methoxy-1-naphthoate, tetradecyl 2-methoxy-1-naphthoate, pentadecyl 2-methoxy-1-naphthoate, hexadecyl 2-methoxy-1-naphthoate, heptadecyl 2-methoxy-1-naphthoate, heptadecyl 2-methoxy-1-naphthoate, octadecyl 2-methoxy-1-naphthoate, nonadecyl 2-methoxy-1-naphthoate, isopropyl 2-methoxy-1-naphthoate, isobutyl 2-methoxy-1-naphthoate, isopentyl 2-methoxy-1-naphthoate, 4-methylpentyl 2-methoxy-1-naphthoate, 5-methylhexyl 2-methoxy-1-naphthoate, 6-methylheptyl 2-methoxy-1-naphthoate, 7-methyloctyl 2-methoxy-1-naphthoate, 8-methylnonyl 2-methoxy-1-naphthoate, 9-methyldecyl 2-methoxy-1-naphthoate, 10-methylundecyl 2-methoxy-1-naphthoate, 11-methyldodecyl 2-methoxy-1-naphthoate, 12-methyltridecyl 2-methoxy-1-naphthoate, 13-methyltetradecyl 2-methoxy-1-naphthoate, 14-methylpentadecyl 2-methoxy-1-naphthoate, 15-methylhexadecyl 2-methoxy-1-naphthoate, 16-methylheptadecyl 2-methoxy-1-naphthoate, 17-methyloctadecyl 2-methoxy-1-naphthoate, and 18-methylnonadecyl 2-methoxy-1-naphthoate, methyl 2-ethoxy-1-naphthoate, methyl 2-propoxy-1-naphthoate, methyl 2-butoxy-1-naphthoate, methyl 2-(pentyloxy)-1-naphthoate, methyl 2-(hexyloxy)-1-naphthoate, methyl 2-(heptyloxy)-1-naphthoate, methyl 2-(octyloxy)-1-naphthoate, methyl 2-(decyloxy)-1-naphthoate, methyl 2-(undecyloxy)-1-naphthoate, methyl 2-(dodecyloxy)-1-naphthoate, methyl 2-(tridecyloxy)-1-naphthoate, methyl 2-(tetradecyloxy)-1-naphthoate, methyl 2-(pentadecyloxy)-1-naphthoate, methyl 2-(hexadecyloxy)-1-naphthoate, methyl 2-(heptadecyloxy)-1-naphthoate, methyl 2-isobutoxy-1-naphthoate, methyl 2-(isopentyloxy)-1-naphthoate, methyl 2-((4-methylpentyl)oxy)-1-naphthoate, methyl 2-((5-methylhexyl)oxy)-1-naphthoate, methyl 2-((6-methylheptyl)oxy)-1-naphthoate, methyl 2-((7-methyloctyl)oxy)-1-naphthoate, methyl 2-((9-methyldecyl)oxy)-1-naphthoate, methyl 2-((10-methylundecyl)oxy)-1-naphthoate, methyl 2-((11-methyldodecyl)oxy)-1-naphthoate, methyl 2-((12-methyltridecyl)oxy)-1-naphthoate, methyl 2-((13-methyltetradecyl)oxy)-1-naphthoate, methyl 2-((14-methylpentadecyl)oxy)-1-naphthoate, methyl 2-((15-methylhexadecyl)oxy)-1-naphthoate, methyl 2-((16-methylheptadecyl)oxy)-1-naphthoate, methyl 2-((16-methylheptadecyl)oxy)-1-naphthoate, methyl 2-((17-methyloctadecyl)oxy)-1-naphthoate, and methyl 2-((18-methylnonadecyl)oxy)-1-naphthoate.
 5. The solid catalyst component according to claim 2, wherein the secondary internal donor compound includes a compound represented by general formula (III) as selected from the group consisting of butyl 2-methoxybenzoate, methyl 2-methoxybenzoate, ethyl 2-methoxybenzoate, propyl 2-methoxybenzoate, pentyl 2-methoxybenzoate, hexyl 2-methoxybenzoate, isopentyl 2-methoxybenzoate, isopropyl 2-methoxybenzoate, isobutyl 2-methoxybenzoate, 4-methylpentyl 2-methoxybenzoate, 5-methylhexyl 2-methoxybenzoate, undecyl 2-methoxybenzoate, tridecyl 2-methoxybenzoate, henicosyl 2-methoxybenzoate, 2-methoxybenzoic acid, butyl 2-hydroxybenzoate, butyl 2-ethoxybenzoate, butyl 2-propoxybenzoate, butyl 2-butoxybenzoate, butyl 2-methoxy-3-methylbenzoate, butyl 2-methoxy-4-methylbenzoate, butyl 2-methoxy-5-methylbenzoate, butyl 2-methoxy-6-methylbenzoate, butyl 3-chloro-2-methoxybenzoate, butyl 5-chloro-2-methoxybenzoate, butyl 4-chloro-2-methoxybenzoate, and butyl 2-chloro-6-methoxybenzoate.
 6. The solid catalyst component according to claim 2, wherein the secondary internal donor compound includes a compound represented by general formula (IV) as selected from the group consisting of methyl 2,6-dimethoxybenzoate, ethyl 2,6-dimethoxybenzoate, propyl 2,6-dimethoxybenzoate, butyl 2,6-dimethoxybenzoate, pentyl 2,6-dimethoxybenzoate, hexyl 2,6-dimethoxybenzoate, heptyl 2,6-dimethoxybenzoate, octyl 2,6-dimethoxybenzoate, nonyl 2,6-dimethoxybenzoate, decyl 2,6-dimethoxybenzoate, dodecyl 2,6-dimethoxybenzoate, octadecyl 2,6-dimethoxybenzoate, phenyl 2,6-dimethoxybenzoate, cyclohexyl 2,6-dimethoxybenzoate, pyridin-4-yl 2,6-dimethoxybenzoate, tetrahydro-2H-pyran-4-yl 2,6-dimethoxybenzoate, isopropyl 2,6-dimethoxybenzoate, isobutyl 2,6-dimethoxybenzoate, isopentyl 2,6-dimethoxybenzoate, 4-methylpentyl 2,6-dimethoxybenzoate, 5-methylhexyl 2,6-dimethoxybenzoate, 6-methylheptyl 2,6-dimethoxybenzoate, 7-methyloctyl 2,6-dimethoxybenzoate, 8-methylnonyl 2,6-dimethoxybenzoate, 9-methyldecyl 2,6-dimethoxybenzoate, butyl 2-ethoxy-6-methoxybenzoate, butyl 2-methoxy-6-propoxybenzoate, 7-methyloctyl 2-ethoxy-6-methoxybenzoate, and 7-methyloctyl 2-methoxy-6-propoxybenzoate.
 7. The solid catalyst component according to claim 2, wherein the secondary internal donor compound includes a compound represented by general formula (V) as selected from the group consisting of (2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (2-ethoxyphenyl)(pyrrolidin-1-yl)methanone, (2-propoxyphenyl)(pyrrolidin-1-yl)methanone, (2-butoxyphenyl)(pyrrolidin-1-yl)methanone, (2-(pentyloxy)phenyl)(pyrrolidin-1-yl)methanone, (2-(hexyloxy)phenyl)(pyrrolidin-1-yl)methanone, (2-(dodecyloxy)phenyl)(pyrrolidin-1-yl)methanone, (2-(icosyloxy)phenyl)(pyrrolidin-1-yl)methanone, (2-isopropoxyphenyl)(pyrrolidin-1-yl)methanone, (2-isobutoxyphenyl)(pyrrolidin-1-yl)methanone, (2-(isopentyloxy)phenyl)(pyrrolidin-1-yl)methanone, (2-phenoxyphenyl)(pyrrolidin-1-yl)methanone, (2-(cyclohexyloxy)phenyl)(pyrrolidin-1-yl)methanone, (2-(pyridin-4-yloxy)phenyl)(pyrrolidin-1-yl)methanone, pyrrolidin-1-yl(2-((tetrahydro-2H-pyran-4-yl)oxy)phenyl)methanone, (2-(2-ethoxyethoxy)phenyl)(pyrrolidin-1-yl)methanone, (2-(2-(ethylamino)ethoxy)phenyl)(pyrrolidin-1-yl)methanone, (2-methoxyphenyl)(2-methylpyrrolidin-1-yl)methanone, (2-chloropyrrolidin-1-yl)(2-methoxyphenyl)methanone, (2-methoxyphenyl)(3-methylpyrrolidin-1-yl)methanone, (3-chloropyrrolidin-1-yl)(2-methoxyphenyl)methanone, (2-methoxy-5-methylphenyl)(pyrrolidin-1-yl)methanone, (2-methoxy-3-methylphenyl)(pyrrolidin-1-yl)methanone, (2-methoxy-4-methylphenyl)(pyrrolidin-1-yl)methanone, (2-methoxy-6-methylphenyl)(pyrrolidin-1-yl)methanone, (5-bromo-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (3-bromo-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (4-bromo-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (2-bromo-6-methoxyphenyl)(pyrrolidin-1-yl)methanone, (5-chloro-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (3-chloro-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (4-chloro-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (2-chloro-6-methoxyphenyl)(pyrrolidin-1-yl)methanone, (5-fluoro-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (3-fluoro-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (4-fluoro-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (2-fluoro-6-methoxyphenyl)(pyrrolidin-1-yl)methanone, (5-iodo-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (3-iodo-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, (4-iodo-2-methoxyphenyl)(pyrrolidin-1-yl)methanone, and (2-iodo-6-methoxyphenyl)(pyrrolidin-1-yl)methanone.
 8. The solid catalyst component according to claim 2, wherein the secondary internal donor compound includes a compound represented by general formula (VI) as selected from the group consisting of dibutyl phthalate (DnBP), diisobutyl phthalate (DIBP), dioctyl phthalate (DOP), bis(2-ethylhexyl) phthalate (DEHP), bis(6-methylheptyl) phthalate (DiOP), bis(7-methyloctyl) phthalate (DINP), and bis(2-propylheptyl) phthalate (DPHP).
 9. The solid catalyst component according to claim 2, wherein the secondary internal donor compound includes a compound represented by general formula (VII) as selected from the group consisting of methyl acetate, ethyl acetate, propyl acetate, butyl acetate, pentyl acetate, hexyl acetate, heptyl acetate, octyl acetate, phenyl acetate, cyclohexyl acetate, isobutyl acetate, isopentyl acetate, 4-methylpentyl acetate, 5-methylhexyl acetate, 6-methylheptyl acetate, 7-methyloctyl acetate, methyl propionate, methyl butyrate, methyl pentanoate, methyl hexanoate, methyl heptanoate, methyl octanoate, methyl decanoate, methyl dodecanoate, methyl stearate, methyl benzoate, methyl cyclohexanecarboxylate, methyl 3-methylbutanoate, methyl 4-methylpentanoate, methyl 5-methylhexanoate, methyl 6-methylheptanoate, methyl 7-methyloctanoate, methyl 9-methyldecanoate, methyl 11-methyldodecanoate, and methyl 16-methylheptadecanoate.
 10. The solid catalyst component according to claim 2, wherein the at least one secondary internal donor compound includes a compound represented by general formula (VIII) as selected from the group consisting of dibutyl cyclohexane-1,2-dicarboxylate, diisobutyl cyclohexane-1,2-dicarboxylate, dioctyl cyclohexane-1,2-dicarboxylate, bis(2-ethylhexyl)cyclohexane-1,2-dicarboxylate, bis(6-methylheptyl)cyclohexane-1,2-dicarboxylate, bis(7-methyloctyl)cyclohexane-1,2-dicarboxylate, bis(5-methyloctyl)cyclohexane-1,2-dicarboxylate, and bis(2-propylheptyl)cyclohexane-1,2-dicarboxylate. 11-12. (canceled)
 13. The solid catalyst component according to claim 1, wherein the titanium compound has at least one titanium-halogen bond and the magnesium compound is a magnesium halide, wherein the magnesium halide forms a crystal lattice, and wherein the combination of internal electron donor compounds are supported on a magnesium halide crystal lattice.
 14. (canceled)
 15. The solid catalyst component according to any claim 1, wherein the titanium compound is TiCl₄ or TiCl₃.
 16. The solid catalyst component according to claim 1 having a surface area (by B.E.T. method) between about 10 and about 1,000 m²/g.
 17. (canceled)
 18. A catalyst system for use in olefinic polymerization, comprising: (i) said solid catalyst component according to claim 1; (ii) an organoaluminum compound; and (iii) optionally an organosilicon compound.
 19. The catalyst system according to claim 18, wherein the organoaluminum compound is an alkyl-aluminum compound.
 20. The catalyst system according to claim 19, wherein the alkyl-aluminum compound is a trialkyl aluminum compound.
 21. (canceled)
 22. The catalyst system of claim 18, wherein the organosilicon compound is present and represented by chemical formula (IX): R_(n)Si(OR′)_(4-n)  (IX) wherein each R and R′ independently represent a hydrocarbon group, and n is an integer from 0 to
 3. 23. The catalyst system of claim 18, where in the organosilicon compound is present and represented by chemical formula (X): SiRR′_(m)(OR″)_(3-m)  (X) wherein R independently represents a cyclic hydrocarbon or substituted cyclic hydrocarbon group, wherein each R′ and R″ independently represent a hydrocarbon group, and wherein m is an integer from 0 to
 2. 24. A process for polymerizing or copolymerizing an olefin monomer, comprising the steps of: (i) providing the catalyst system of claim 18; (ii) polymerizing or copolymerizing the olefin monomer in the presence of the catalyst system to form a polymer or a copolymer; and (iii) recovering the polymer or copolymer.
 25. The process according to claim 24, wherein the olefin monomer is selected from the group consisting of ethylene, propylene, 1-butene, 1-methyl-1-pentene, 1-hexene, and 1-octene. 